明胶溶液中针状纳米HgS的仿生合成

doi:10.7517/j.issn.1674-0475.2008.03.200

影像科学与光化学 ›› 2008, Vol. 26 ›› Issue (3): 200-205.DOI: 10.7517/j.issn.1674-0475.2008.03.200

明胶溶液中针状纳米HgS的仿生合成

唐世华, 黄在银

广西民族大学化学与生态工程学院, 广西, 南宁530006

收稿日期:2007-10-18 修回日期:2007-12-27 出版日期:2008-05-23 发布日期:2008-05-23
基金资助:
广西省自然科学基金(0728056);广西民族大学重大科研项目(民大[2006]24号)

Biomimetic Synthesis of Acicular Nanometer HgS in the Gelatin Solution

TANG Shi-hua, HUANG Zai-yin

College of Chemistry and Ecological Engineering, Guangxi University for Nationalities, Nanning 530006, Guangxi, P. R. China

Received:2007-10-18 Revised:2007-12-27 Online:2008-05-23 Published:2008-05-23

摘要/Abstract

摘要： 以明胶为模板剂,制备出在明胶水溶液中稳定存在的HgS微晶.通过扫描电镜(SEM)图像表明,生长时间为2d的样品为微晶结构,生长15d的HgS微晶为针状,平均直径约87nm,长度约1.3μm.紫外可见吸收和荧光光谱的测试结果表明,所合成HgS具有量子限域效应.明胶分子的构象变化对HgS纳米颗粒的成核和形貌转化起到非常重要的作用.

关键词: 硫化汞, 针状纳米粒子, 明胶, 仿生合成

Abstract: HgS acicular nanocrystals conjugated with gelatin were successfully synthesized in aqueous solution of gelatin at room temperature. SEM images showed that when the reaction time reached 2 d, the particles of HgS was formed while the reaction time reached 15 d, the particles turned into the acicular nanoparticles. The average diameter of the acicular nanoparticles was 87 nm with the length of 1.3 μm. The quantum-confined effect of the HgS nanoparticles was confirmed by the ultraviolet-visible and fluorescence spectrum. The results indicate that the change of gelatin conformation not only induce the nucleation, but is favorable to the pattern change of HgS nanoparticles.

Key words: mercury sulfide, acicular nanoparticles, gelatin, biomimetic synthesis

中图分类号:

TQ57

唐世华, 黄在银. 明胶溶液中针状纳米HgS的仿生合成[J]. 影像科学与光化学, 2008, 26(3): 200-205.

TANG Shi-hua, HUANG Zai-yin. Biomimetic Synthesis of Acicular Nanometer HgS in the Gelatin Solution[J]. Imaging Science and Photochemistry, 2008, 26(3): 200-205.

参考文献

[1] Service R F.Nanomaterials show signs of toxicity[J].Science,2003,300:243.
[2] 唐世华,黄在银,黄建滨.明胶溶液中笤帚状纳米CdS的合成及其光谱特性研究[J].化学学报,2007,65:1432-1436.Tang S H,Huang Z Y,Huang J B.Synthesis and spectral properties of broom-like CdS nanoparticles in gelatin solution[J].Acta Chim.Sinica,2007,65:1432-1436.
[3] 翁诗甫.傅立叶变换红外光谱仪[M].北京:化学工业出版社,2005.320-326.Weng S F.Foutier Transform Infrared Spectrometer[M].Beijing:Chemical Industry Press,2005.320-326.
[4] 严金龙,聂福礼,王肇福.鞣性金属-明胶固体络合物的红外光谱[J].皮革化工,1998,15:8-11.Yan J L,Nie F L,Wang Z F.Infrared spectra of solid complexes of gelatin and its tanning metal[J].Leather Chem.,1998,15:8-11.
[5] 郭尧君.荧光实验技术及其在分子生物学中的应用[M].北京:科学出版社,1979.128.Guo Y J.The Application of Experimental Technology of Fluorescence in Molecular Biology[M].Beijing:Science Press,1979.128.
[6] 韩峭峰,孙明,余林,余倩,余坚.复合掺杂的纳米二氧化锡粒子的制备与表征[J].无机盐工业,2007,39:13-15.Han Q F,Sun M,Yu L,Yu Q,Yu J.Synthesis and characterization of composite-doped SnO₂ nanoparticles[J].Inorg.Chem.Industry,2007,39:13-15.
[7] Chakraborty I,Mitra D,Moulik S P.Spectroscopic studies on nanodispersions of CdS,HgS,their core-shells and composites prepared in micellar medium[J].J.Nanopart.Res.,2005,7:227-236.
[8] 贾润萍,杨俊和,吴庆生,丁亚平,李永胜,欧阳春发,王霞.活性生物膜模板法诱导控制合成硫化汞纳米网状结构[J].兰州大学学报(自然科学版),2007,43:58-60.Jia R P,Yang J H,Wu Q S,Ding Y P,Li Y S,OuYang C F,Wang X.Biomimetic synthesis of web-linked mercury sulfide[J].J.Lanzhou.Univ.(Nat.Sci.),2007,43:58-60.
[9] 蒋治良,蒙冕武,刘绍璞.黄色硫化镉纳米粒子的共振瑞利散射光谱研究[J].分析化学,2003,31:315-317.Jiang Z L,Mcng M W,Liu S P.Resonance Rayleigh scettering spectroscopy of yellow CdS nanoparticle[J].Chinese J.Anal.Chem.,2003,31:315-317.
[10] Qin D Z,Ma X M,Yang L,Zhang L,Ma Z J,Zhang J.Biomimetic synthesis of HgS nanoparticles in the bovine serum albumin solution[J].J.Nanopart.Res.,DOI 10.1007/sl1051-007-9284-9.

[1]	王毅虎, 曹霄峰, 张兵, 王佳宁, 张炜杰, 郭燕川. 甲基丙烯酰胺基明胶水凝胶研究进展[J]. 影像科学与光化学, 2020, 38(1): 22-26.
[2]	纪海侠, 董露露, 杜岩, 姚欣悦, 杨冬芝. 肿瘤细胞内CdS纳米量子点的仿生化合成[J]. 影像科学与光化学, 2018, 36(1): 57-63.
[3]	王毅虎, 张兵, 马铭, 卢伟鹏, 王佳宁, 郭燕川. 紫外光共聚交联制备GelMA/PEGDA水凝胶[J]. 影像科学与光化学, 2017, 35(4): 574-580.
[4]	邓秋, 黎幼群, 唐世华. 纳米ZnS与明胶蛋白质的相互作用[J]. 影像科学与光化学, 2016, 34(4): 336-345.
[5]	王白杨, 肖新光, 唐世华, 刘岑. 明胶/Fe₂S₃纳米生物复合物形成反应的热力学及明胶构象变化[J]. 影像科学与光化学, 2014, 32(6): 505-513.
[6]	马铭, 王雪松, 张兵, 郭燕川. 明胶溶液中沉淀法制备纯相β-磷酸三钙[J]. 影像科学与光化学, 2012, 30(4): 269-279.
[7]	姜小明, 宋磊, 赵濉. 荧光探针法研究双子型阳离子表面活性剂与明胶的相互作用[J]. 影像科学与光化学, 2012, 30(3): 175-181.
[8]	张兵, 史京京, 王颖, 郭燕川, 陈丽娟. 酸预处理对酶法骨明胶功能性质和分子质量分布的影响[J]. 影像科学与光化学, 2012, 30(2): 102-109.
[9]	肖新光, 黎幼群, 唐世华. 纳米硫化钴与明胶蛋白质的原位键合作用研究[J]. 影像科学与光化学, 2011, 29(4): 297-305.
[10]	葛军, 孙瑞雪, 史京京, 张兵, 陈丽娟. 戊二醛交联前后明胶微球热转变研究[J]. 影像科学与光化学, 2009, 27(5): 334-341.
[11]	孙瑞雪, 郭燕川, 张兵, 陈丽娟, 陈大福, 石锐, 周新华. 明胶/羟基磷灰石复合物微球中明胶对无机相影响的研究[J]. 影像科学与光化学, 2009, 27(5): 342-350.
[12]	田宝柱, 童天中, 陈锋, 张金龙. 明胶对纳米二氧化钛相变和光催化活性的影响[J]. 影像科学与光化学, 2006, 24(2): 93-101.
[13]	唐世华. 同步荧光光谱法研究明胶蛋白质与铜 (Ⅱ)的相互作用[J]. 影像科学与光化学, 2005, 23(2): 102-107.
[14]	李东芹, 黄碧霞, 岳军, 周涛. 明胶与Ag⁺相互作用的XPS研究[J]. 影像科学与光化学, 2004, 22(3): 169-174.
[15]	刘霁, 宋磊, 岳军. 纳米尺度AgBr/I乳剂颗粒的光电子衰减行为[J]. 影像科学与光化学, 2004, 22(2): 81-87.

明胶溶液中针状纳米HgS的仿生合成

Biomimetic Synthesis of Acicular Nanometer HgS in the Gelatin Solution

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价