混杂光固化体系的原理及应用

doi:10.7517/j.issn.1674-0475.2001.03.208

影像科学与光化学 ›› 2001, Vol. 19 ›› Issue (3): 208-216.DOI: 10.7517/j.issn.1674-0475.2001.03.208

混杂光固化体系的原理及应用

陈明, 陈其道, 肖善强, 洪啸吟

清华大学化学系, 北京100084

收稿日期:2000-12-01 修回日期:2001-02-05 出版日期:2001-08-20 发布日期:2001-08-20
通讯作者: 洪啸吟(1938-),男,教授,博士生导师,主要从事功能高分子材料的研究;通讯联系人,E-mail:hongxy@mail.tsinghua.edu.cn
基金资助:
国家自然科学基金资助项目(20074021)

THE MECHANISM AND APPLICATION OF HYBRID UV CURING SYSTEM

CHEN Ming, CHEN Qi-dao, XIAO Shan-qiang, HONG Xiao-yin

Department of Chemistry, Tsinghua University, Beijing 100084, P. R. China

Received:2000-12-01 Revised:2001-02-05 Online:2001-08-20 Published:2001-08-20

摘要/Abstract

摘要： 混杂光固化或双重固化是指在同一体系中采用两种或两种以上不同类型的聚合反应来使体系固化的方法,它是原位改性高分子的一种新方法.混杂光固化体系包括自由基-阳离子混杂光固化体系、自由基-缩聚混杂体系和自由基-自由基混杂体系等.本文综述了混杂光固化体系的原理及其应用.

关键词: 紫外光固化, 混杂聚合, 阳离子光固化, 双重固化

Abstract: Hybrid UV curing or dual curing consists of two or more kinds of polymerization or crosslinking reactions that take place in the same system, which is a novel approach to modify polymer materials in-situ. Hybrid UV curing system includes free radical-cationic hybrid UV curing system, Free radical-condensation polymerization system and free radical-free radical system. The mechanism and application of hybrid UV curing are reviewed in this paper.

Key words: UV curing, hybrid, polymerization, cationic UV curing, dual curing

中图分类号:

O644

陈明, 陈其道, 肖善强, 洪啸吟. 混杂光固化体系的原理及应用[J]. 影像科学与光化学, 2001, 19(3): 208-216.

CHEN Ming, CHEN Qi-dao, XIAO Shan-qiang, HONG Xiao-yin. THE MECHANISM AND APPLICATION OF HYBRID UV CURING SYSTEM[J]. Imaging Science and Photochemistry, 2001, 19(3): 208-216.

参考文献

[1] Fouassier J P, Rabek J F. Radiation Curing in Polymer Science an d Technology [M]. Vol. 1. New York: Elsevier Applied Science, 1993.1-47.
[2] Fouassier J P, Rabek J F. Radiation Curing in Polymer Science an d Technology [M]. Vol. 3. New York: Elsevier Applied Science, 1993.177-217.
[3] Crivello J V, Lam J H W. Cationic polymerization of epoxide resin [J]. Macromolecules, 1977,10(6):1307-1315. ④ Ryoji Nishioka, Jiyi Oka. Study on composite paint film cured by combi nation of electron beam and thermal energy. Radtech Asia '91 Radiation curing co nference, Osaka: RadTech Asia, 1991, 104-108.
[4] Pappas S P. Photoinitiation of cationic and concurrent radical-ca tionic polymerization [J] , Part V. J. Imag. Technol., 1985,11(4):146.
[5] Pappas S P. UV Curing: Science and Technology [M]. Vol. 2. C onnecticut: Technology Marketing Corporation, 1985.1-25.
[6] Fouassier J P, Rabek J F. Radiation Curing in Polymer Science an d Technology [M]. Vol. 2. New York: Elsevier Applied Science, 1993.435-471.
[7] He J H, Mendoza V S. Synthesis and study of a novel hybrid UV phot oinitiator: p-benzoyldiphenyliodonium hexafluorophosphate [J]. J. Polym . Sci., Part A, 1996,34(13):2809-2816.
[8] 潘才元.膨胀聚合反应及其应用[M].成都:四川教育出版社,1988.1.Pan C Y. The Reaction and Application of Expanding Polymerization [M]. Che ngdu: Sichuan Education Press, 1988.1.
[9] Bailey W J, et al. Synthesis of monomer that expand on polymer ization [C]. ACS Symp. Ser.59, 1977,38-59.
[10] 哄啸吟,冯汉保.涂料化学.北京:科学出版社,1997.176-198.Hong X Y, Feng H B. Coating Chemistry. Beijing: Scientific Press, 199 7.176-198.
[11] Nativi L A. Adhesive and sealing compositions [P]. US Patent, 4 415 604. 1983-08-27.
[12] Skinner E. Liquid chemical waste destruction [P]. US Patent, 4 128 000. 1978-12-20.
[13] 陈士杰.涂料工艺(第一分册)[M].北京:化学工业出版社,1996.645-7 56.Chen S J. The Techniques of Coatings [M]. Vol. 1. Beijing: Chemical En gineering Press, 1996.645-756.
[14] 洪啸吟,余荣阵,张雷,等.六(甲氧甲基)三聚氰氨/多元醇二甲基丙烯酸酯的混合聚合体系[J].高分子学报,1993,3:277-281.Hong X Y, Yu Y Z, Zhang L, et al. HMMM/poyol dimethylacrylate hy brid polymerization system [J]. Acta Polymerica Sinica, 1993,3 :277-281.
[15] 陆企亭.快固型胶粘剂(合成胶粘剂丛书第七册)[M].北京:科学出版社 ,1992.118-137.Lu Q T, Fast Curing Adhesive (Synthesis Adhesive. Vol. 7)[M]. Beijing: Sci entific Press, 1992.118-137.
[16] Nativi L A. Conformal coating systems [P]. US Patent, 4 451 523.1984-03-27.

混杂光固化体系的原理及应用

THE MECHANISM AND APPLICATION OF HYBRID UV CURING SYSTEM

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	刘通政, 王勇, 薛探龙, 王涛. 含巯基MTQ树脂的合成及对丙烯酸酯体系光固化性能的影响[J]. 影像科学与光化学, 2019, 37(5): 456-464.
[2]	张娜, 陈媛, 聂俊, 杨金梁. 光固化阳离子活性稀释剂研究进展[J]. 影像科学与光化学, 2016, 34(6): 491-504.
[3]	张变香, 史瑞雪, 亢永强, 李婷婷. 新型苯基苯并噻吩酮光引发剂的合成及应用[J]. 影像科学与光化学, 2016, 34(6): 534-540.
[4]	万时策, 黄笔武, 杜志鹏, 雍涛, 韩文娟. 新型阳离子光固化活性单体3,3'-[1,4-丁基双(氧基亚甲基)]-双-(3-乙基)氧杂环丁烷的合成[J]. 影像科学与光化学, 2016, 34(2): 181-189.
[5]	钱夏庆, 王德海, 李恒. 单体结构对紫外光固化氧阻聚影响的研究[J]. 影像科学与光化学, 2013, 31(4): 276-285.
[6]	刘红波, 林峰, 肖望东, 徐玲, 张武英. 有机硅改性丙烯酸环氧单酯光-热混杂固化体系的表面性能[J]. 影像科学与光化学, 2013, 31(2): 125-131.
[7]	张洪, 李建雄, 刘安华. 阳离子光引发剂敏化的研究进展[J]. 影像科学与光化学, 2013, 31(1): 69-78.
[8]	蔡万泼, 王德海, 盛伟明. 紫外光固化材料热老化黄变的研究[J]. 影像科学与光化学, 2012, (5): 390-397.
[9]	吕建波. PET光学膜紫外光固化硬涂层的制备[J]. 影像科学与光化学, 2011, 29(6): 449-455.
[10]	刘世民, 黄笔武, 程桂亮. 乙二醇二缩水甘油醚的合成及作为阳离子型紫外光固化稀释剂性能研究[J]. 影像科学与光化学, 2011, 29(6): 456-463.
[11]	翁子骧, 黄笔武, 郑雪琳, 姜安坤. 活性稀释剂苄基缩水甘油醚丙烯酸酯的合成及性能表征[J]. 影像科学与光化学, 2011, 29(2): 140-148.
[12]	欧霄巍, 聂俊, 何勇. 一种低分子量带有羧基的聚丙烯酸酯丙烯酸树脂的制备和性质[J]. 影像科学与光化学, 2010, 28(3): 182-192.
[13]	夏朝荣, 刘仁, 黄强, 张胜文, 江金强, 刘晓亚. 大分子阳离子光引发剂聚苯乙烯-碘鎓六氟锑酸盐的合成及其感光性能的研究[J]. 影像科学与光化学, 2008, 26(6): 438-444.
[14]	宋家乐, 陈立新, 王亚洲, 王汝敏, 张教强. 巯基/乙烯基硅氮烷紫外光固化的研究[J]. 影像科学与光化学, 2008, 26(3): 218-223.
[15]	徐冬梅, 张可达, 宁春花, 朱秀林. 紫外光快速固化的树枝状丙烯酸酯齐聚物的制备和性能[J]. 影像科学与光化学, 2004, 22(4): 287-292.