The Preparation of Ag Loaded Nanotube Titanic Acid Catalyst

doi:10.7517/j.issn.1674-0475.2008.02.104

Abstract

Abstract: The Ag loaded nanotube titanic acid was prepared by the photo-reduction method. The photograph of TEM showed that Ag particles deposited on the surface of the nanotube titanic acid. Results of XPS and XRD indicated that the Ag⁺ was reduced to metal. The results of photodegradation of methylene blue showed that the photocatalytic activity of Ag loaded nanotube titanic acid was higher than that of the nanotube titanic acid.

Key words: nanotube titanic acid, Ag, surface-loaded, methylene blue, photocatalytic degradation

CLC Number:

O643

MA Xin-qi, FENG Cai-xia, GUI Li-li, YAO-Li, NIU Yu-qi, GUO Xin-yong. The Preparation of Ag Loaded Nanotube Titanic Acid Catalyst[J]. Imaging Science and Photochemistry, 2008, 26(2): 104-108.

References

[1] Asahi R,Morikawa T,Ohwaki T,et al.Visible-light photocatalysisin nitrogen-doped titaniumoxides[J].Science,2001,293:269-271.
[2] Ye WY,Cheng T F,Ye Q,et al.Preparation and tribological properties of tetrafluorobenzoic acid-modified TiO₂nanoparticles as lubrican additives[J].Materials Science and Engineering,2003,359:82-85.
[3] Jianli Y,Phillip E S.Kinetics of catalytic supercritical water oxidation of phenol over TiO₂[J].Environ.Sci.Tech-nol.,2000,34:3191-3198.
[4] Lin C H,Lin YC,Chang C L,et al.Photodecomposition of methylene-blue by highly-dispersed nano TiO₂/Agcata-lyst[J].Reaction Kinetics and Catalysis Letters,2007,90(2):267-273.
[5] Arabatzis I M,Stergiopoulos T,Bernard M C,et al.Silver-modified titanium dioxide thin fil ms for efficient pho-todegradation of methyl orange[J].Applied Catalysis B:Environmental,2003,42(1):187-201.
[6] Shi L P,Li C Z,Chen AP,et al.Morphological structure of nanometer TiO₂-Al₂O₃composite powders synthesized in high temperature gas phase reactor[J].Chemical EngineeringJournal,2001,84:405-411.
[7] 尤先锋,陈锋,张金龙,等.银促进的TiO₂光催化降解甲基橙[J].催化学报,2006,27(3):270-274.You X F,Chen F,Zhang J L,et al.Photocatalytic degradation of methyl orange on TiO₂promoted by silver[J].Chinese Journal of Catalysis,2006,27(3):270-274.
[8] Zhang M,Jin Z S,ZhangJ W,et al.Effect of annealingtemperature on morphology,structure and photocatalytic be-havior of nanotubed H₂Ti2O4(OH)2[J].J.Mol.Cata.A:Chem.,2004,217:203-210.
[9] 王克,张敏,金振声,等.负载金的纳米管钛酸光催化氧化一氧化碳[J].催化学报,2005,26(4):283-286.Wang K,Zhang M,Jin Z S,et al.Photocatalytic oxidation of carbon monoxide on Au-loaded nanotube titanic acid[J].Chinese Journal of Catalysis,2005,26(4):283-286.
[10] Ma X Q,Feng C X,Jin Z S,et al.Insertion of platinumoxide into nanotube of sodiumtitanate[J].Journal of Nanoparticle Research,2005,7(6):681-683.
[11] Yang J J,Jin Z S,Wang X D,et al.Study on composition,structure and formation process of nanotube Na₂Ti₂O₄(OH)₂[J].Dalton Transactions,2003,20:3898-3901.
[12] 马新起,郭新勇,金振声,等.纳米管钛酸和二氧化钛的暗态吸附性能[J].化学研究,2004,15(4):14-16.Ma X Q,Guo X Y,Jin Z S,et al.Di madsorption property of nanotube of titanic acid andtitania[J].Chemical Re-search,2004,15(4):14-16.
[13] 甘礼华,陈龙武,胜文超,等.TiO₂薄膜制备及其对亚甲基蓝光催化降解的影响[J].建筑材料学报,2003,6(3):274-278.Gan L H,Chen L W,Sheng WC,et al.Preparation of TiO₂functional fil mandits effect on photocatalysis degrada-tion of methylene blue[J].Journal of Building Matereals,2003,6(3):274-278.
[14] Einaga H.Effect of silver deposition ontiofor photocatalytic oxidation of benzeneinthe gas phase[J].Reaction Ki-netics and Catalysis Letters,2006,88(2):357-362.
[15] 邢铁玲,Chu K H,陈国强.亚甲基蓝的超声化学降解[J].印染,2005,(23):13-15.Xing T L,Chu K H,Chen G Q.Sonochemical degradation of methylene blue in aqueous solution[J].Dyeing and Finishing,2005,(23):13-15.
[16] 段春英,周静芳.银纳米颗粒的制备与表征[J].化学研究,2003,14(3):18-20.Duan C Y,Zhou J F.Preparation and characterization of silver nanoparticle[J].Chemical Research,2003,14(3):18-20.