可聚合型光引发剂4-丙烯酰氧基二苯甲酮的光聚合性能研究

doi:10.7517/j.issn.1674-0475.2008.01.32

影像科学与光化学 ›› 2008, Vol. 26 ›› Issue (1): 32-38.DOI: 10.7517/j.issn.1674-0475.2008.01.32

可聚合型光引发剂4-丙烯酰氧基二苯甲酮的光聚合性能研究

张海清¹, 肖浦², 戴明之¹, 何勇¹, 聂俊^1,2

1. 北京化工大学, 材料科学与工程学院, 新型高分子材料制备与加工北京市重点实验室, 北京, 100029;
2. 武汉大学, 化学与分子科学学院, 生物医用高分子教育部重点实验室, 湖北, 武汉, 430072

收稿日期:2007-06-20 修回日期:2007-07-29 出版日期:2008-01-23 发布日期:2008-01-23
通讯作者: 聂俊,E-mail:niejun@mail.buct.edu.cn.

Photopolymerization of 4-Acryloylbenzophenone

ZHANG Hai-qing¹, XIAO Pu², DAI Ming-zhi¹, HE Yong¹, NIE Jun^1,2

1. The Key Laboratory of Beijing City on Preparation and Processing of Novel Polymer Materials, College of Material Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, P. R. China;
2. Key Laboratory of Biomedical Polymers of Ministry of Education, Department of Chemistry, Wuhan University, Wuhan 430072, Hubei, P. R. China

Received:2007-06-20 Revised:2007-07-29 Online:2008-01-23 Published:2008-01-23

摘要/Abstract

摘要： 以实时红外光谱(RT-IR)法研究了合成的4-丙烯酰氧基二苯甲酮(4-ABP)的光聚合动力学性质,考察了不同单体、不同引发剂和助引发剂浓度、不同光强对聚合性能的影响.以萃取法对比研究了4-ABP和二苯甲酮(BP)在固化膜中的的残留量.结果表明,4-ABP是一种非常有效的光引发剂.随着引发剂浓度和光强的增大,单体转化率、最大反应速率都增大,诱导期缩短.萃取实验表明4-ABP在固化膜中的残留量远低于BP.

关键词: 可聚合光引发剂, 可萃性, 光聚合, 动力学, RT-IR

Abstract: The kinetics of photopolymerization of 4-acryloylbenzophenone (4-ABP) was studied by Real-time Infrared spectroscopy,which showed that 4-ABP was a very effective photoinitiator.When the photoinitiator and amine were used to initiate polymerization of acrylates,both rate of polymerization and final conversion increased and the induction period shortened with increase of amine concentration,4-ABP concentration and light intensity.For it is crosslinked in the cured film,the amount of extracted 4-ABP is much lower than that of BP.

Key words: polymerizable photoinitiator, photopolymerization, kinetics, extractability, RT-IR

中图分类号:

张海清, 肖浦, 戴明之, 何勇, 聂俊. 可聚合型光引发剂4-丙烯酰氧基二苯甲酮的光聚合性能研究[J]. 影像科学与光化学, 2008, 26(1): 32-38.

ZHANG Hai-qing, XIAO Pu, DAI Ming-zhi, HE Yong, NIE Jun. Photopolymerization of 4-Acryloylbenzophenone[J]. Imaging Science and Photochemistry, 2008, 26(1): 32-38.

参考文献

[1] 肖浦,吴刚强,史素青,等.基于α-羟烷基苯酮(HAPK)可聚合大分子光引发剂的合成及其引发三丙二醇双丙烯酸酯(TPGDA)光聚合动力学的研究[J].感光科学与光化学(影像科学与光化学),2006,5:204-210.Xiao P,Wu G Q,Shi S Q,et al.Synthesis of macrophotoinitiator based On HAPK and kinetics for photopolymerization of TPGDA[J].Photographic Science and Photochemistry(Imaging Science and Photochemistry),2006,5:204-210.
[2] Juan S,Norman A.Photochemistry and photoinduced chemical crosslinking activity of several type Ⅱ commercial photoinitiators in acrylated prepolymers[J].Journal of Photochemistry and Photobiology A:Chemistry,1999,122:115-125.
[3] 魏杰,金养智.光固化涂料[M].北京:化学工业出版社,2005.59-60.Wei J,Jin Y Z.UV-curable Coatings[M].Beijing:Chemical Industry Press,2005.59-60.
[4] 陈用烈,曾兆华,杨建文.辐射固化材料及其应用[M].北京:化学工业出版社,2003.130-142.Chen Y L,Zeng Z H,Yang J W.Radiant-curable Materials and Application[M].Beijing:Chemical Industry Press,2003.130-142.
[5] Wu G Q,Nie J.Synthesis and characterization of aliphatic amine co-initiator with different chain length for photopolymerization of dimethacrylate[J].Journat of Photochemistry and Photobiology A:Chemistry,2007,188:260-266.
[6] 金日光,华幼卿.高分子物理[M].第二版.北京:化学工业出版社,2000.103-112.JIn R G,Hua Y Q.Polymer Physics[M].2nd ed.Beijing:Chemical Industry Press,2000.103-112.
[7] Yu Q,Naurmm S,Smterte J P.UV photopolymerization behavior of dimethacrylate oligomers with eamphorquinone/amine initiator system[J].J.Appl.Polym.Sci.,2001,82(5):1107-1117.
[8] Decker C,Jenkins A D.Kinetic approach of oxygen inhibition in ultraviolet-and laser-induced polymerizations[J].Macromolecules,1985,18(6):1241-1244.

[1]	王辉, 周文秀. 彩色多普勒超声对自体动静脉内瘘成熟度的评估作用研究[J]. 影像科学与光化学, 2020, 38(6): 967-970.
[2]	纪亚梅, 蔡腾. 头颅超声检测脑血流动力学对新生儿缺血缺氧性脑病的筛查价值[J]. 影像科学与光化学, 2020, 38(6): 1027-1031.
[3]	范少平, 安模, 杨波, 吕春潮, 梁碧先, 黎姣. 彩色多普勒超声在高血压脑出血显微手术及围术期脑血流动力学监测中的应用价值[J]. 影像科学与光化学, 2020, 38(6): 1056-1060.
[4]	胡祥午, 朱晓群, 聂俊, 王涛, 许延卿, 刘瑶. 连续光聚合制备环氧基微球及表面功能化[J]. 影像科学与光化学, 2020, 38(5): 771-779.
[5]	陈尚雄, 唐洁, 杜松, 张辉, 孙龙, 刘平, 牟玮, 郝迎学. 血管内支架介入对老年症状性椎动脉狭窄的疗效分析[J]. 影像科学与光化学, 2020, 38(4): 671-675.
[6]	高洋, 苏嘉辉, 刘晓暄. 基于UV-LED茂铁盐体系对脂环族环氧单体的阳离子光聚合动力学研究[J]. 影像科学与光化学, 2020, 38(2): 190-199.
[7]	周金娣, 陆炳宇. 4-乙烯基-1-环己烯二环氧化物阳离子单体光聚合性能研究[J]. 影像科学与光化学, 2020, 38(1): 37-45.
[8]	李星洲, 侯尊岩, 何勇. 超临界二氧化碳光聚合制备可交联含氟聚合物颗粒及应用[J]. 影像科学与光化学, 2019, 37(5): 392-401.
[9]	庞玉莲, 赵丽英, 高明, 邹应全. 适用于UV-LED光源的新型光引发剂的合成及其性能研究[J]. 影像科学与光化学, 2019, 37(5): 438-444.
[10]	谢刚, 杨建文, 钟荣. 氟碳链修饰酰基氧化膦长波吸收光引发剂的研究[J]. 影像科学与光化学, 2018, 36(5): 389-397.
[11]	陈利, 吴青阳, 刘仁, 李治全. 高稳定性巯-烯体系的深层光聚合研究[J]. 影像科学与光化学, 2018, 36(5): 408-416.
[12]	董晓庆, 李治全, 刘仁, 刘晓亚. 基于光致脱羧的单组分可见光引发剂的合成及其光化学性能研究[J]. 影像科学与光化学, 2018, 36(3): 226-235.
[13]	李聪, 张荣金, 袁妍, 刘仁. 离子液体-脲基嘧啶酮混合型低收缩率单体的制备及应用[J]. 影像科学与光化学, 2018, 36(3): 254-266.
[14]	尹祥祥, 王磊, 聂俊, 杨金梁. 一种新型二苯甲酮类光引发剂的合成及其性能研究[J]. 影像科学与光化学, 2018, 36(2): 200-209.
[15]	郑美玲, 金峰, 董贤子, 赵圆圆, 赵震声, 段宣明. 双光子光聚合与功能微纳结构制备[J]. 影像科学与光化学, 2017, 35(4): 413-428.

可聚合型光引发剂4-丙烯酰氧基二苯甲酮的光聚合性能研究

Photopolymerization of 4-Acryloylbenzophenone

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价