Zn-TiO2/AC复合催化剂的制备及其光催化活性

doi:10.7517/j.issn.1674-0475.2004.04.266

影像科学与光化学 ›› 2004, Vol. 22 ›› Issue (4): 266-271.DOI: 10.7517/j.issn.1674-0475.2004.04.266

Zn-TiO₂/AC复合催化剂的制备及其光催化活性

吴遵义, 杜玉扣, 华南平, 沈明, 杨平

苏州大学化学化工学院, 江苏, 苏州, 215006

收稿日期:2003-11-17 修回日期:2004-02-23 出版日期:2004-07-23 发布日期:2004-07-23
通讯作者: 杨平
基金资助:
国家自然科学基金(90207026)

Preparation and Photocatalytic Activity of Zn-TiO₂/AC Catalysts

WU Zun-yi, DU Yu-kou, HUA Nan-ping, SHEN Ming, YANG Ping

Department of Chemistry of Suzhou University, Suzhou 215006, Jiangsu, P.R. China

Received:2003-11-17 Revised:2004-02-23 Online:2004-07-23 Published:2004-07-23

摘要/Abstract

摘要： 以硝酸锌、钛酸四丁酯和活性炭为原料,采用真空吸附法制备了不同组成的Zn TiO₂/AC.通过X射线衍射(XRD)和透射电镜(TEM)对催化剂进行了表征.选择较难降解的Cl₃CCOOH作为探针分子考察了其光催化活性.结果表明,掺锌能提高TiO₂/AC的催化活性,当Zn的摩尔分数为0.5%(相对TiO₂)、处理温度为400℃,溶液的pH值为6时,Zn TiO₂/AC催化剂具有很好的光催化活性.

关键词: TiO₂, Zn掺杂, 活性炭, 光催化活性, 三氯乙酸光降解

Abstract: The supported photocatalyst TiO₂/AC doping with Zn²⁺ was prepared by means of vacuum absorption-hydrolysis method.The catalyst was characterized by XRD and TEM.The photocatalytic activity of samples was evaluated by the photodegradation of Cl₃CCOOH.The result shows that the photocatalytic activities were significantly increased when the supported catalyst was doped with Zn²⁺ at optimal concentration (0.5 at.%).The highest photodegradation activity Cl₃CCOOH can be reached under condition of Zn-TiO₂/AC catalyst treated at 400 ℃ for 2 hours and pH=6 for the reaction solution.

Key words: TiO₂, Zn-doping, actived carbon, photodegradation, trichloroacetic acid

中图分类号:

吴遵义, 杜玉扣, 华南平, 沈明, 杨平. Zn-TiO₂/AC复合催化剂的制备及其光催化活性[J]. 影像科学与光化学, 2004, 22(4): 266-271.

WU Zun-yi, DU Yu-kou, HUA Nan-ping, SHEN Ming, YANG Ping. Preparation and Photocatalytic Activity of Zn-TiO₂/AC Catalysts[J]. Imaging Science and Photochemistry, 2004, 22(4): 266-271.

参考文献

[1] Fujishima A,Honda K. Electrochemical photolysis of water at a semiconductor electrode[J]. Nature, 1972,237:37-38.
[2] 孙奉玉,吴鸣,等二氧化钛的活性表面与光催化的关系[J].催化学报,1998,19(2):121-124.Sun F Y,Wu M, et al. Relationship between optical surface and photocatalytic activity of titanium dioxide[J]. Chinese Journal of Catalysis, 1998,19(2): 121-124.
[3] 高廉,郑珊,张青红纳米二氧化钛光催化材料及应用[M].北京:化学工业出版社,2002.Gao L, Zhen S,Zhang Q H. Photocatalytic material and application of nano-titania[M]. Beijing: Chemical Industry Press, 2002.
[4] 陆诚,杨平,杜玉扣,华南平载体对负载型TiO₂催化剂光催化性能的影响[J].催化学报,2003,24(4):248-252.Lu C, Yang P, Du Y K, Hua N P. Effect of support on photocatalytic performance of supported TiO₂ catalysts[J]. Chinese Journal of Catalysis, 2003,24 (4): 248-252.
[5] 尹峰,林瑞峰,林原,肖绪瑞TiO₂表面电子结构及其光催化活性[J].催化学报,1999,20(3):343-346.Yin F,Lin R F,Lin Y,Xiao X R. The surface of electronic structure and photocatalytic activity of TiO₂[J]. Chinese Journal of Catalysis, 1999,20(3): 343-346.
[6] Yang P, Lu C, Hua N P, Du Y K. Tatiana dioxide nanoparticles co-doped with Fe³⁺ and Eu³⁺ ions for photocatalysis[J].Materials Letters, 2002,14 (5): 794-801.
[7] 李太友,刘琼玉,刘延湘.TiO₂-Fenton试剂光氧化降解水中氯代有机物的研究[J]环境科学与技术,2001增刊:1-3.Li T Y, Liu Q Y, Liu Y X. The photodegradation of chlorinated organic compounds in water by TiO₂-Fenton systems[J].Environ. Sci. Tech., 2001 supplement: 1-3.
[8] 陆诚,杨平,杜玉扣,华南平.Fe³⁺/V⁵⁺TiO₂复合纳米微粒光催化性能研究[J].化学研究与应用,2002,14(3):265-268.Lu C, Yang P, Du Y K, Hua N P. Study on photocatalysis of Fe³⁺/V⁵⁺/TiO₂ nanometer particles[J]. Investigation and Application in Chemistry, 2002,14(3): 265-268.
[9] 李卫华,乔学斌,高恩勤,杨迈之,等.3d过渡金属掺杂TiO₂纳米晶膜电极的光化学研究[J].高等学校化学学报,2000,21(10):1534-1538.Li W H,Qiao X B,Gao E Q,Yang M Z, et al. Photoeletrochemical behavior of 3d transition metal nanostructured film electrode doped with TiO₂[J]. Chemical Journal of Chinese University, 2000,21 (10): 1534-1538.
[10] Yuan Z H,Jia J H,Zhang L D. Influence of co-doping of Zn(Ⅱ) + Fe(Ⅲ) on the photocatalyticactivity of TiO₂ for phenol degradation, materials[J]. Chemistry and Physics, 2002,73: 323-326.

[1]	李玥, 李红英, 常玉雪, 周宏艳, 于翔. MoS₂/TiO₂纳米管阵列的一步沉积法制备及光电性能研究[J]. 影像科学与光化学, 2018, 36(4): 331-339.
[2]	俞洁, 慈明珠, 鲁泉玲, 马舒晴, 姜丽, 雷菊英, 刘勇弟, 张金龙. TiO₂反蛋白石光子晶体最新研究进展[J]. 影像科学与光化学, 2018, 36(1): 14-32.
[3]	张国强, 曲丹, 苗湘, 张晓燕, 孙再成. CdS超薄片层包覆TiO₂中空结构复合材料的形成和应用[J]. 影像科学与光化学, 2015, 33(5): 374-382.
[4]	史丽娜, 曲阳, 李志君, 孙莉群, 井立强. TiO₂/Bi₂O₃纳米复合体的制备及可见光催化产氢性能[J]. 影像科学与光化学, 2015, 33(5): 426-433.
[5]	张纪伟, 金振声, 张经纬, 李秋叶, 张治军. 富含本征缺陷的新型锐钛矿TiO₂纳米管的制备[J]. 影像科学与光化学, 2015, 33(4): 285-291.
[6]	李秋叶, 金振声. 可见光“全”分解水的类纳光电化学(PEC)电池模型[J]. 影像科学与光化学, 2015, 33(2): 99-107.
[7]	张鹏, 于彦龙, 匡元江, 姚江宏, 曹亚安. Si掺杂TiO₂催化剂的结构与可见光催化活性研究[J]. 影像科学与光化学, 2013, 31(4): 295-304.
[8]	韩严和, 姜金海, 蒋丽, 李宝琴, 刘璐, 陈家庆, 梁存珍. 阴离子对TiO₂晶形的影响及光催化性能研究[J]. 影像科学与光化学, 2013, 31(3): 186-196.
[9]	费学宁, 刘星星, 李金蕊, 姜远光. 磁功能性TiO₂光催化剂的制备及特性[J]. 影像科学与光化学, 2013, 31(3): 229-237.
[10]	袁静, 安振国, 张敬杰, 李冰. 空心玻璃微珠/TiO₂复合微球的制备及其性能研究[J]. 影像科学与光化学, 2012, 30(6): 447-455.
[11]	余明光, 陈广学, 陈奇峰, 黄文涛, 屈贞财, 朱志伟. TiO₂光致亲水性及其在免处理版材中的应用研究[J]. 影像科学与光化学, 2012, 30(1): 71-77.
[12]	景明俊, 王岩, 张敏, 杨建军. 负载金的掺氮二氧化钛的制备及其可见光催化性能[J]. 影像科学与光化学, 2011, 29(5): 353-363.
[13]	孟丹, 王和义, 刘秀华, 丁兰岚, 胥全敏. 低含量铁掺杂纳米TiO₂薄膜的制备及其抗菌机理研究[J]. 影像科学与光化学, 2011, 29(4): 306-314.
[14]	阮修莉, 邵冬海. TiO₂纳米管电极金属离子掺杂的表征[J]. 影像科学与光化学, 2011, 29(1): 54-62.
[15]	曹静, 林海莉, 罗邦德, 李辰, 陈士夫. 异质结型AgI/AgBr/TiO₂催化剂的制备及其光催化性能[J]. 影像科学与光化学, 2010, 28(5): 334-342.

Zn-TiO₂/AC复合催化剂的制备及其光催化活性

Preparation and Photocatalytic Activity of Zn-TiO₂/AC Catalysts

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价