传统化学增感对PVA为粘合剂的光敏热成像材料的光敏性的影响

doi:10.7517/j.issn.1674-0475.2005.02.108

影像科学与光化学 ›› 2005, Vol. 23 ›› Issue (2): 108-113.DOI: 10.7517/j.issn.1674-0475.2005.02.108

传统化学增感对PVA为粘合剂的光敏热成像材料的光敏性的影响

曹静^1,2, 林海莉^1,2, 姚林辉¹, 史瑶¹, 李金培¹, 夏培杰¹

1. 中国科学院, 理化技术研究所, 北京, 100101;
2. 中国科学院, 研究生院, 北京, 100039

收稿日期:2004-11-08 修回日期:2004-12-17 出版日期:2005-03-23 发布日期:2005-03-23
通讯作者: 夏培杰,研究员,E-mail:xpj@mail.ipc.ac.cn.
基金资助:
国家自然科学青年基金资助项目(20303025).

Effects of Conventional Chemical Sensitizations on Sensitivity of PTG Materials Using PVA as a Hydrophilic Binder

CAO Jing^1,2, LIN Hai-li^1,2, YAO Lin-hui¹, SHI Yao¹, LI Jin-pei¹, XIA Pei-jie¹

1. Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100101, P.R. China;
2.Graduate School of Chinese Academy of Sciences, Beijing 100039, P.R. China

Received:2004-11-08 Revised:2004-12-17 Online:2005-03-23 Published:2005-03-23

摘要/Abstract

摘要： 以水性聚乙烯醇 (PVA)为粘合剂,以异位法制备的颗粒尺寸为140nm的AgBr乳剂作光敏元,考察了传统化学增感方法对PTG材料的光敏性影响.实验结果表明,分别将经过硫增感、金增感、硫加金增感以及还原增感的AgBr乳剂加入到PTG体系中,均提高了PTG体系的光敏性,而灰雾却没有明显的增长.

关键词: 光敏热成像材料, 干银, 卤化银, 化学增感

Abstract: The conventional chemical sensitizations (sulfur-, gold, sulfur-plus-gold and reduction-sensitization) were used to sensitize the AgBr emulsions with about 140 nm of grain size, covered in PTG coating with PVA as a binder, in order to examine the effects on sensitivities of PTG materials. The results showed that the chemical sensitizations were still quite effective for PTG system with hydrophilic PVA to increase sensitivities significantly, but not fog levels.

Key words: Photothermographic materials, dry silver, silver halide, chemical sensitization

中图分类号:

TQ57

曹静, 林海莉, 姚林辉, 史瑶, 李金培, 夏培杰. 传统化学增感对PVA为粘合剂的光敏热成像材料的光敏性的影响[J]. 影像科学与光化学, 2005, 23(2): 108-113.

CAO Jing, LIN Hai-li, YAO Lin-hui, SHI Yao, LI Jin-pei, XIA Pei-jie. Effects of Conventional Chemical Sensitizations on Sensitivity of PTG Materials Using PVA as a Hydrophilic Binder[J]. Imaging Science and Photochemistry, 2005, 23(2): 108-113.

参考文献

[1] Whitcomb D R. 基于羧酸银的光敏热成像技术进展[J]. 感光科学与光化学, 2003,21 (1): 1-19.Whitcomb D R. Advances in photothermographic imaging technology based on silver carboxylates[J].Photographic Science and Photochemistry, 2003,21 (1): 1-19.
[2] David A Morgan. Heat-developable photographic silver salt material[P]. BE patent, 663 112, 1965.
[3] Irving M E, Levy D H, Reynolds J H, et al. Packaged color photographic film capable of alternatively dry or wet-chemical processing[P]. WO patent, 0 196 950, 2001.
[4] Zou C, Sahyun M R V, Levy B, et al. Mechanisms of latent image formation in photothermographic silver imaging media[J].J. Imag. Sci. Technol., 1996.40:94-103.
[5] 曹静, 林海莉, 姚林辉, 智欣, 李金培, 夏培杰. AgBr的尺寸及含量对PVA为粘合剂的光敏热成像材料的光敏性的影响[J].感光科学与光化学, 2005, 23 (1):6-13.Cao J, Lin H L, Yao L H, Zhi X, Li J P, Xia P J. Effects of grain size and content of AgBr on sensitivity of PTG materials using PVA as a hydrophilic binder[J]. Photographic Science and Photochemistry, 2005, 23 (1):6-13.
[6] Reeves J W. Photothermographic silver halide material and process[P]. US patent,4 435 499, 1984.
[7] Bolshakov V N, Goryave M A. Apparatus and recording medium for rapid computer output of half tone images[J].Opt. Tekh. Prom, 1991, 11: 68-73.
[8] Gisser K R C, Eshelman L M, Irving M E, Levy D H. Process of preparing a photothermographic composition of enhanced photosensitivity[P]. US patent, 5 858 637, 1999.
[9] Gisser K R C, Eshelman L M, Irving M E, Levy D H. Photothermographic composition of enhanced photosensitivity and a process for its preparation[P]. US patent, 5 843 632, 1998.
[10] Sahyun M R V.Thermally Developable Photographic Materials (TDPM):A review of the state-of-the-art in mechanistic understanding[J]. J. Imag. Sci. Technol., 1998,42:23-30.
[11] Featherstone G L, Lynch D C, Miller J R, Skimmer M C, Windolw J M,Simpson S M. Chemical sensitization of photothermographic silver halide emulsions[P]. US patent, 5 891 615, 1999.
[12] Katsutoshi Yamane, Seiji Yamashita. The role of silver halides in photothermographic materials with a water dispersible binder[C]. In:Inter. Conf. Imaging Sci.,Japan: Tokyo,2002.29-30.

[1]	李秋艳, 权莹, 梁海燕, 张乐. 化学增感对苯并三氮唑银的PTG材料感光性能的影响[J]. 影像科学与光化学, 2015, 33(3): 218-223.
[2]	聂宜文, 张兴业, 宋延林. 单分散性银纳米粒子的可控制备[J]. 影像科学与光化学, 2014, 32(4): 402-409.
[3]	李秋艳, 李剑, 马望京, 李金培. 不同光敏剂对光敏热成像材料感光性能的影响[J]. 影像科学与光化学, 2014, 32(2): 209-215.
[4]	梁海燕, 李秋艳, 李姝静, 王心蕊, 叶宏, 李金培. 提高光敏热成像材料感光性能的研究进展[J]. 影像科学与光化学, 2012, 30(4): 308-317.
[5]	李秋艳, 孙双月, 梁海燕, 李金培. 混合银盐的光敏热成像材料感光性能研究[J]. 影像科学与光化学, 2012, 30(1): 53-59.
[6]	李秋艳, 李金培. 两种不同银源的光敏热成像材料感光性能对比[J]. 影像科学与光化学, 2010, 28(4): 254-264.
[7]	李秋艳, 李金培. 4-羟基-6-甲基-1,3,3a,7-四氮茚对以苯并三氮唑银为银源的PTG材料感光性能的影响[J]. 影像科学与光化学, 2009, 27(2): 111-120.
[8]	李智, 段培成, 杨新民, 郑彤. 反相微乳液法制备纳米Ag₂S增感剂的化学增感研究[J]. 影像科学与光化学, 2008, 26(5): 385-392.
[9]	曹静, 林海莉, 刘春萍, 王俊恩, 邵新. AgSt/AgBr复合物的制备及其热行为研究[J]. 影像科学与光化学, 2008, 26(4): 265-270.
[10]	林海莉, 曹静, 姚林辉, 李金培, 夏培杰. Pb²⁺和Zn²⁺对亲水型光敏热成像材料感光性能和存储稳定性能的影响[J]. 影像科学与光化学, 2008, 26(3): 211-217.
[11]	曹静, 林海莉, 姚林辉, 夏培杰. 光敏热成像材料的化学增感进展[J]. 影像科学与光化学, 2007, 25(4): 311-317.
[12]	林海莉, 马望京, 姚林辉, 夏培杰, 李金培. 甲酸和草酸盐掺杂的AgBr乳剂对亲水型PTG材料感光性能的影响[J]. 影像科学与光化学, 2007, 25(2): 102-109.
[13]	李智, 郑彤, 史京京, 王颖, 彭必先, 陈丽娟. 氯化银立方体微晶乳剂和{100}面扁平微晶乳剂的甲酸盐掺杂增感[J]. 影像科学与光化学, 2006, 24(5): 343-350.
[14]	范明明, 邹竞, 王虹. 光敏热显成像材料概述[J]. 影像科学与光化学, 2006, 24(2): 140-151.
[15]	曹静, 林海莉, 姚林辉, 史瑶, 夏培杰. 苯并三氮唑在聚乙烯醇为粘合剂的光敏热成像材料中的化学增感[J]. 影像科学与光化学, 2005, 23(5): 351-356.

传统化学增感对PVA为粘合剂的光敏热成像材料的光敏性的影响

Effects of Conventional Chemical Sensitizations on Sensitivity of PTG Materials Using PVA as a Hydrophilic Binder

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价