酸化对层状K2La2Ti3O10光催化活性的影响

doi:10.7517/j.issn.1674-0475.2004.02.120

影像科学与光化学 ›› 2004, Vol. 22 ›› Issue (2): 120-125.DOI: 10.7517/j.issn.1674-0475.2004.02.120

酸化对层状K₂La₂Ti₃O₁₀光催化活性的影响

李涛海, 吴季怀, 林建明, 程应汉

华侨大学, 材料物理化学研究所, 福建, 泉州, 362011

收稿日期:2003-11-10 修回日期:2004-01-05 出版日期:2004-03-23 发布日期:2004-03-23
通讯作者: 吴季怀
基金资助:
国家自然科学基金资助项目(50082003,50372022);福建省国际合作项目(2001I006);福建省自然科学基金资助项目(E0210023)

THE INFLUENCE OF ACIDIFICATION ON PHOTOCATALYTIC PROPERTY OF LAYERED K₂La₂Ti₃O₁₀

LI Tao-hai, WU Ji-huai, LIN Jian-ming, CHENG Ying-han

Institute of Materials Physics and Chemistry, Huaqiao University, Quanzhou 362011, Fujian, P.R. China

Received:2003-11-10 Revised:2004-01-05 Online:2004-03-23 Published:2004-03-23

摘要/Abstract

摘要： 本文通过高温固相反应合成了一种层状金属氧化物K₂La₂Ti₃O₁₀,利用离子交换反应对其在不同条件下进行酸化.并通过对甲基橙溶液的降解对其光催化活性进行评价,结果发现,酸化后K₂La₂Ti₃O₁₀的光催化活性有显著提高.通过对样品的结构、XRD、DRS分析,对这种现象做出了几种可能的解释.

关键词: 层状K₂La₂Ti₃O₁₀, 离子交换反应, 光催化, 降解

Abstract: Photocatalytic degradation of methyl orange over a kind of layered metaloxide was accomplished.K₂La₂Ti₃O₁₀,a layered perovskite-type compound with a 1.39 nm interlayer space,exhibited a low activity for methyl orange decomposition.The notable activity was obtained when K₂La₂Ti₃O₁₀ was acidified in 2 mol/L HNO₃ solution.

Key words: layered K₂La₂Ti₃O₁₀, photocatalytic, acidification, methyl orange

中图分类号:

O643

李涛海, 吴季怀, 林建明, 程应汉. 酸化对层状K₂La₂Ti₃O₁₀光催化活性的影响[J]. 影像科学与光化学, 2004, 22(2): 120-125.

LI Tao-hai, WU Ji-huai, LIN Jian-ming, CHENG Ying-han. THE INFLUENCE OF ACIDIFICATION ON PHOTOCATALYTIC PROPERTY OF LAYERED K₂La₂Ti₃O₁₀[J]. Imaging Science and Photochemistry, 2004, 22(2): 120-125.

参考文献

[1] Kenji Toda,Toshihiko Honma, Ye Zuo-Guang, et al. Synthesis and structure determination of new layered perovskite compound KLaTa₂O₇[J].Journal of Alloys and compounds,1997,249(10):256-259.
[2] Wu Jihuai,Satoshi Uchida, Yoshinobu Fujishiro, et al. Synthesis and photocatalyticproperties of HTaWO₆/(Pt,TiO₂)and HTaWO₆/(Pt, Fe₂O₃) nanocomposites[J]. International Journal of Inorganic Materials, 1999,97(1):253-258.
[3] Wu J H, Satoshi Uchida, Yoshinobu Fujishiro, et al. Synthesis and photocatalytic properties of HNbWO₆/TiO₂ and HNbWO₆/Fe₂O₃ nanocompsites[J]. Journal of Photochemistry and Photobiology A: Chemistry, 1999,128(11): 129-133.
[4] Takata T,Shinohara K,Tanaka A, Hara M,et al. A highly active photocatalyst for overall water splitting with a hydrated layered perovskite structure[J]. Journal of Photochemistry and Photobiology A: Chemistry, 1997,106(3):45-49.
[5] Tsuyoshi Takata, Yoko Furumi, Kiyoaki Shinohara, et al. Photocatalytic decomposition of water on spontaneously hydrated layered perovskites[J]. Chem. Mater., 1997,9 (2): 1063-1064.
[6] Thaminimulla C T K, Takata T, Hara M, Kondo J N, et al. Effect of chromium addition for photocatalytic overall water splitting on Ni-K₂La₂Ti₃O₁₀[J]. Journal of Catalysis, 2000,196(8): 362-365.
[7] 吴季怀,林煜,黄妙良,等.层状纳米光催化复合材料HNbWO₆/Pt的合成及性质[J].催化学报,2001,22(2):209-211.Wu J H, Ling Y,Huang M L, et al. Synthesis and property of HNbWO₆/Pt layered nanocomposite photocatalyst[J].Chinese Journal of Catalysis, 2001,22 (2): 209-211.
[8] 陈亚芍,候文华,颜其洁.氧化铝柱层状镧钛酸盐的制备[J].无机化学学报,1995,11(4):399-403.Cheng Y S,Hou W H, Yan Q J. Synthesis of alumina-pillared layered lanthanum titanate[J]. Journal of Inorganic Chemistry, 1995,11 (4): 399-403.
[9] 王恩波,胡长文.多酸化学导论[M].北京:化学工业出版社,1998 120-122.Wang E B, Hu C W. Introduction of Polyoxometalates Chemistry[M]. Beijing: Chemical Industry Press, 1998,120-122.

[1]	李玥, 李红英, 常玉雪, 周宏艳, 于翔. MoS₂/TiO₂纳米管阵列的一步沉积法制备及光电性能研究[J]. 影像科学与光化学, 2018, 36(4): 331-339.
[2]	李玥, 宋育泽, 陶雁忠, 高风仙, 汤宁. CdS/TiO₂复合纳米网的制备及光催化性能研究[J]. 影像科学与光化学, 2018, 36(3): 275-282.
[3]	李玲, 杜云舒, 王璇, 韩建, 王传义. 甲醛气体在ZnO表面光降解的机理研究[J]. 影像科学与光化学, 2018, 36(2): 171-177.
[4]	吴世康. 光催化中表面等离子体与半导体间的电子转移与能量转移[J]. 影像科学与光化学, 2018, 36(1): 1-13.
[5]	贾智慧, 李玉虎, 石美荣, 谢丽娜, 周亚军. 馆库温湿度对醋酸纤维素酯胶片物理性能影响的研究[J]. 影像科学与光化学, 2017, 35(6): 797-807.
[6]	Samuel Lascio, 籍海峰. 磷纳米材料的光学、光电子和光催化应用[J]. 影像科学与光化学, 2017, 35(5): 587-602.
[7]	张庆宝, 刘强. 可见光催化需氧氧化在有机合成中的应用[J]. 影像科学与光化学, 2017, 35(5): 614-625.
[8]	桂梦茜, 俞洋, 朱诚逸, 刘宏芳, 王锋. 基于金属钴配合物的均相光催化还原二氧化碳研究进展[J]. 影像科学与光化学, 2017, 35(5): 649-657.
[9]	彭成云, 陈勇. 苝衍生物光催化氧化硫醚的研究[J]. 影像科学与光化学, 2017, 35(5): 675-685.
[10]	聂坤, 杨汉培, 孙慧华, 崔素珍, 吴俊明. 新型Fe掺杂钙钛矿型KMgF₃光催化剂制备及性能[J]. 影像科学与光化学, 2017, 35(1): 61-69.
[11]	朱哲欣, 叶美英. 光催化微反应器中水样光催化降解及Cd²⁺在线检测[J]. 影像科学与光化学, 2016, 34(5): 444-451.
[12]	张亚婷, 李可可, 任绍昭, 王黛玉, 周安宁, 邱介山. 金属改性煤基石墨烯复合材料的制备及其光催化性能[J]. 影像科学与光化学, 2016, 34(5): 475-481.
[13]	王勐, 夏静, 朱丹丹, 王磊, 孟祥敏. Fe掺杂ZnO空心微球的制备与光催化性能[J]. 影像科学与光化学, 2016, 34(3): 245-251.
[14]	蒋伟, 武祥. ZnS微米花的水热合成及光催化性质研究[J]. 影像科学与光化学, 2016, 34(3): 252-256.
[15]	黄奔, 李玄泽, 王磊, 夏静, 朱丹丹, 孟祥敏. 钼网衬底上大面积硅纳米线的制备及其光催化性能研究[J]. 影像科学与光化学, 2016, 34(3): 257-264.

酸化对层状K₂La₂Ti₃O₁₀光催化活性的影响

THE INFLUENCE OF ACIDIFICATION ON PHOTOCATALYTIC PROPERTY OF LAYERED K₂La₂Ti₃O₁₀

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价