二氧化钛包裹碘单质(I2/TiO2)制备及其光催化降解苯酚

doi:10.7517/j.issn.1674-0475.2009.03.198

摘要/Abstract

摘要： 采用水热法,以Ti(SO₄)₂为钛源,KIO₃为掺碘剂制备了具有高可见光活性,高稳定性的二氧化钛包裹碘单质(I₂/TiO₂)光催化剂.利用X射线光电子能谱(XPS)、X射线晶体粉末衍射(XRD)、透射电子显微镜(TEM)和紫外可见漫反射光谱(DRS)等表征手段对样品进行表征.结果表明,I₂/TiO₂中除含有锐钛矿相二氧化钛外、还含有碘单质和碘酸;I₂/TiO₂粒径大小为45 nm左右;在波长384 nm至700 nm范围内,该催化剂有强烈的吸收.探讨了该催化剂的形成过程和可见光催化机理.以苯酚降解反应为探针,测定了I₂/TiO₂光催化活性.结果显示:在全谱光源照射下I₂/TiO₂活性略高于P25,在可见光范围内其活性是P25的3倍多.确定了降解苯酚的最佳条件:全谱光源照射,投加量为0.5 g/L,苯酚浓度大于10 mg/L,溶液pH为3.2.I₂/TiO₂重复使用4次后,催化活性没有明显下降.

关键词: TiO₂, 碘掺杂, 光催化, 苯酚降解

Abstract: A simple method for preparing highly visible-light photocatalytic activity and stability nanocrystalline (I₂)_n encapsulation inside TiO₂(I₂/TiO₂) powders was developed by a mild hydrothermal route.The as-prepared TiO₂ powders were characterized by X-ray diffraction(XRD),UV-vis diffuse reflectance spectra(DRS) and transmission electron microscopy (TEM).XRD and TEM measurement revealed that HIO₃ and I₂ existed in I₂/TiO₂,the size of I₂/TiO₂ was about 45.0 nm.I₂/TiO₂ exhibited obvious a strong absorption in the range of wavelengths from 384 to 700 nm.The formation process of I₂/TiO₂ and a possible mechanism for the photocatalysis on I₂/TiO₂ under visible light were proposed.Photocatalytic activity test by degradation of phenol,I₂/TiO₂ showed much better photocatalytic activity than P25. The conditions of degradation of phenol were optimized as follows: full-spectrum light illumination,quantity of catalysts is 0.5 g/L,initial concentration of phenol is 10 mg/L,the pH of solution is 3.2.

Key words: TiO₂, iodine doped, photocatalytic, degradation of phenol

中图分类号:

邓培昌, 王海增, 樊丽霞, 孙宝维. 二氧化钛包裹碘单质(I₂/TiO₂)制备及其光催化降解苯酚[J]. 影像科学与光化学, 2009, 27(3): 198-206.

DENG Pei-chang, WANG Hai-zeng, FAN Li-xia, SUN Bao-wei. Preparation of(I₂)_n Encapsulation Inside TiO₂ and Photocatalytic Degradation of Phenol[J]. Imaging Science and Photochemistry, 2009, 27(3): 198-206.

参考文献

[1] Young C,Li m T M,Chiang K,et al.Photocatalytic oxidation of toluene and trichloroethylene in the gas-phase bymetallised(Pt,Ag)titaniumdioxide[J].Appl.Catal.,B,2008,78:1-10.
[2] Liu J J,Li X P,Zuo S L,et al.Preparation and photocatalytic activity of silver and TiO₂ nanoparticles/montmorill-onite composites[J].Appl.Clay Sci.,2007,37:275-280.
[3] 柳丽芬,李秀婷,杨凤林,等.Ag/TiO₂ 光催化氧化还原反应脱除水体中无机氮[J].感光科学与光化学(影像科学与光化学),2006,24:291-300.Liu L F,Li X T,Yang F L,et al.Nitrogen removal via ammonia oxidation and nitrite reduction using Ag/TiO₂ andphotocatalysis[J].Photographic Science and Photochemistry(Imaging Science and Photochemistry),2006,24:291-300.
[4] Ki m D H,Lee KS,Ki m Y S,et al.Photocatalytic activity of Ni 8 wt%-doped TiO₂ photocatalyst synthesized bymechanical alloying under visible light[J].J.Am.Ceram.Soc.,2006,89(2):515-518.
[5] Jiang HQ,Wang P,Guo X L,et al.Preparation and characterization of low-amount Yb³⁺-doped TiO₂ photocatalyst[J].Russ.Chem.Bull.Int.Edit.,2006,55(10):1743-1747.
[6] Ki m D H,Hong HS,Ki mS J,et al.Photocatalytic behaviors and structural characterization of nanocrystalline Fe-doped TiO₂ synthesized by mechanical alloying[J].J.Alloys Compd.,2004,375:259-264.
[7] Zhu A M,Nie L H,Zhang X L,et al.Anewapproachto plasma CVDof TiO₂ photocatalyst onγ-Al₂O₃ pellet filledin dielectric barrier discharges at atmospheric pressure[J].Plasma Sci.Technol.,2004,6(6):2546-2548.
[8] Arai Y,Tanaka K,Khlaifat AL.Photocatalysis of SiO₂-loaded TiO₂ [J].J.Mol.Catal.A:Chem.,2006,243:85-88.
[9] Jin Z L,Zhang XJ,Li Y X,et al.5.1%apparent quantumefficiencyfor stable hydrogen generation over eosin-sen-sitized CuO/TiO₂ photocatalyst under visible light irradiation[J].Catal.Commun.,2007,8:1267-1273.
[10] Ozcan O,Yukruk F,Akkaya E U,et al.Dye sensitized artificial photosynthesisinthe gas phase over thin andthickTiO₂ fil ms under UVand visible light irradiation[J].Appl.Catal.,B:Environmental,2007,71:291-297.
[11] Iwasaki M,Hara M,Kawada H,et al.Cobalt Ion-doped TiO₂ photocatalyst response to visible light[J].J.Col-loidInterface Sci.,2000,224:202-204.
[12] Jiang H Q,Wang P,Guo X L,et al.Preparation and characterization of low-amount Yb³⁺-doped TiO₂ photo-catalyst[J].Russ.Chem.Bull.,International Edition,2006,55(10):1743-1747.
[13] Ki m D H,Lee KS,Ki m Y S,et al.Photocatalytic activity of Ni 8 wt%-doped TiO₂ photocatalyst synthesized bymechanical alloying under visible light[J].J.Am.Ceram.Soc.,2006,89(2):515-518.
[14] Xu X H,Wang M,Hou Y,et al.Preparation and characterization of Bi-doped TiO₂ photocatalyst[J].J.Mater.Sci.Lett.,2002,21:1655-1656.
[15] Moon J,Takagi H,Fujishiro Y,et al.Preparation and characterization of the Sb-doped TiO₂ photocatalysts[J].J.Mater.Sci.,2001,36:949-955.
[16] Sato S.Photocatalytic activity of NOx-doped TiO₂ inthe visiblelight region[J].Chem.Phys.Lett.,1986,123(1-2):126-128.
[17] Asahi R,Morikawa T,Ohwaki T,et al.Visible-light photocatalysis in nitrogen-doped titaniumoxides[J].Sci.,2001,293:269-271.
[18] Chen S F,Chen L,Gao S,et al.The preparation of nitrogen-doped photocatalyst TiO_2-xN_x by ball milling[J].Chemical Physics Letters,2005:404-409.
[19] Yin S,Ihara K,Aita Y,et al.Visible-light induced photocatalytic activity of TiO_2-xA_y (A=N,S)prepared byprecipitation route[J].Journal of Photochemistry and Photobiology A:Chemistry,2006,179:105-114.
[20] Janus M,Inagaki M,Tryba B,et al.Carbon-modified TiO₂ photocatalyst by ethanol carbonization[J].AppliedCatalysis B:Environmental,2006,63:272-276.
[21] Li D,Haneda H,Hishita S,et al.Fluorine-doped TiO₂ powders prepared by spray pyrolysis and their i mprovedphotocatalytic activity for decomposition of gas-phase acetaldehyde[J].J.Fluorine Chem.,2005,126:69-77.
[22] Luo H M,Takata T,Lee Y,et al.Photocatalytic Activity enhancing for titanium dioxide by co-doping withbromine and chlorine[J].Chem.Mater.,2004,16:846-849.
[23] Hong X T,Wang Z P,Cai W M,et al.Visible-light-activated nanoparticle photocatalyst of iodine-doped titaniumdioxide[J].Chem.Mater.,2005,17:1548-1552.
[24] Liu G,Chen Z G,Dong C L,et al.Visiblelight photocatalyst:iodine-doped mesoporoustitania with a bicrystallineframework[J].J.Phys.Chem.,B,2006,110:20823-20828.
[25] Su WY,Zhang Y F,Li Z H,et al.Multivalency iodine doped TiO₂:preparation,characterization,theoreticalstudies,and visible-light photocatalysis[J].Langmuir,2008,24:3422-3428.
[26] Usseglio S,Damin A,Scarano D,et al.(I₂)_nencapsulationinside TiO₂:a way to tune photoactivityin the visibleregion[J].J.Am.Chem.Soc.,2007,129:2822-2828.
[27] 胡春,王怡中,汤鸿霄.TiO₂ 光催化氧化苯酚动力学研究[J].环境科学,1997,15(4):472-479.Hu C,Wang YZ,Tang HX.Kinetics of photocatalytic oxidation of phenol on TiO₂ [J].Environ.Sci.,1997,15(4):472-479.

二氧化钛包裹碘单质(I₂/TiO₂)制备及其光催化降解苯酚

Preparation of(I₂)_n Encapsulation Inside TiO₂ and Photocatalytic Degradation of Phenol

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	李玥, 李红英, 常玉雪, 周宏艳, 于翔. MoS₂/TiO₂纳米管阵列的一步沉积法制备及光电性能研究[J]. 影像科学与光化学, 2018, 36(4): 331-339.
[2]	李玥, 宋育泽, 陶雁忠, 高风仙, 汤宁. CdS/TiO₂复合纳米网的制备及光催化性能研究[J]. 影像科学与光化学, 2018, 36(3): 275-282.
[3]	李玲, 杜云舒, 王璇, 韩建, 王传义. 甲醛气体在ZnO表面光降解的机理研究[J]. 影像科学与光化学, 2018, 36(2): 171-177.
[4]	吴世康. 光催化中表面等离子体与半导体间的电子转移与能量转移[J]. 影像科学与光化学, 2018, 36(1): 1-13.
[5]	俞洁, 慈明珠, 鲁泉玲, 马舒晴, 姜丽, 雷菊英, 刘勇弟, 张金龙. TiO₂反蛋白石光子晶体最新研究进展[J]. 影像科学与光化学, 2018, 36(1): 14-32.
[6]	Samuel Lascio, 籍海峰. 磷纳米材料的光学、光电子和光催化应用[J]. 影像科学与光化学, 2017, 35(5): 587-602.
[7]	张庆宝, 刘强. 可见光催化需氧氧化在有机合成中的应用[J]. 影像科学与光化学, 2017, 35(5): 614-625.
[8]	桂梦茜, 俞洋, 朱诚逸, 刘宏芳, 王锋. 基于金属钴配合物的均相光催化还原二氧化碳研究进展[J]. 影像科学与光化学, 2017, 35(5): 649-657.
[9]	彭成云, 陈勇. 苝衍生物光催化氧化硫醚的研究[J]. 影像科学与光化学, 2017, 35(5): 675-685.
[10]	聂坤, 杨汉培, 孙慧华, 崔素珍, 吴俊明. 新型Fe掺杂钙钛矿型KMgF₃光催化剂制备及性能[J]. 影像科学与光化学, 2017, 35(1): 61-69.
[11]	朱哲欣, 叶美英. 光催化微反应器中水样光催化降解及Cd²⁺在线检测[J]. 影像科学与光化学, 2016, 34(5): 444-451.
[12]	张亚婷, 李可可, 任绍昭, 王黛玉, 周安宁, 邱介山. 金属改性煤基石墨烯复合材料的制备及其光催化性能[J]. 影像科学与光化学, 2016, 34(5): 475-481.
[13]	王勐, 夏静, 朱丹丹, 王磊, 孟祥敏. Fe掺杂ZnO空心微球的制备与光催化性能[J]. 影像科学与光化学, 2016, 34(3): 245-251.
[14]	蒋伟, 武祥. ZnS微米花的水热合成及光催化性质研究[J]. 影像科学与光化学, 2016, 34(3): 252-256.
[15]	黄奔, 李玄泽, 王磊, 夏静, 朱丹丹, 孟祥敏. 钼网衬底上大面积硅纳米线的制备及其光催化性能研究[J]. 影像科学与光化学, 2016, 34(3): 257-264.