一种新型的交联极化聚合物的合成及性能研究

doi:10.7517/j.issn.1674-0475.2007.06.452

影像科学与光化学 ›› 2007, Vol. 25 ›› Issue (6): 452-458.DOI: 10.7517/j.issn.1674-0475.2007.06.452

一种新型的交联极化聚合物的合成及性能研究

赵文轲^1,2, 王志鹏^1,2, 陈卓^1,2, 徐光明¹, 韩旭¹, 邱玲¹, 甄珍¹, 刘新厚¹

1. 中国科学院, 理化技术研究所, 北京, 100080;
2. 中国科学院, 研究生院, 北京, 100049

收稿日期:2007-03-22 修回日期:2007-05-14 出版日期:2007-11-23 发布日期:2007-11-23
通讯作者: 刘新厚,E-mail:xhliu@mail.ipc.ac.cn.
基金资助:
国家自然科学基金资助项目(20374058);中国科学院知识创新工程重要方向性项目(KJCX3.5YW.H02)

Synthesis and Properties of a Novel Cross-Linked Poled Polymer

ZHAO Wen-ke^1,2, WANG Zhi-peng^1,2, CHEN Zhuo^1,2, XU Guang-ming¹, HAN Xu¹, QIU Ling¹, ZHEN Zhen¹, LIU Xin-hou¹

1. Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100080, P. R. China;
2. Graduate University of the Chinese Academy of Sciences, Beijing 100049, P. R. China

Received:2007-03-22 Revised:2007-05-14 Online:2007-11-23 Published:2007-11-23

摘要/Abstract

摘要： 以成膜性能优异、主链上含有多个羟基的聚双酚A二缩水甘油醚-苯胺(BPAN)为骨架,将二阶非线性光学活性发色团分子以键合形式挂接到聚合物主链上,形成新型侧链型聚合物.此聚合物保留了原聚合物体系成膜性好和可进一步交联等优点.极化过程中以含有异氰酸酯基的同种发色团分子作为交联剂,得到发色团含量进一步提高的交联型极化聚合物.采用衰减全反射法(ATR)测得体系的电光系数(r₃₃)为6.7 pm/V(1315 nm).

关键词: 极化聚合物, 交联, 二阶非线性光学, 电光系数, 衰减全反射

Abstract: A novel NLO side-chain polymer was synthesized by attaching the NLO chromophore to a hydroxy-containing polymer BPAN which possesses excellent processability.The new polymer inherited the good performance of BPAN such as good film formation property and cross-linkability,etc.Cross-linked poled polymer with even higher content of NLO chromophore was obtained by taking the same kind of NCO-containing chromophore as cross-linking agent.The electro-optic coefficient of the poled polymer was 6.7 pm/V,which was measured by ATR method at 1315 nm.

Key words: poled polymer, cross-linking, NLO, EO, Attenuated Total Reflection(ATR)

中图分类号:

赵文轲, 王志鹏, 陈卓, 徐光明, 韩旭, 邱玲, 甄珍, 刘新厚. 一种新型的交联极化聚合物的合成及性能研究[J]. 影像科学与光化学, 2007, 25(6): 452-458.

ZHAO Wen-ke, WANG Zhi-peng, CHEN Zhuo, XU Guang-ming, HAN Xu, QIU Ling, ZHEN Zhen, LIU Xin-hou. Synthesis and Properties of a Novel Cross-Linked Poled Polymer[J]. Imaging Science and Photochemistry, 2007, 25(6): 452-458.

参考文献

[1] Meredith G R,VanDusen J,Williams D J.Optical and nonlinear optical characterization of molecularly doped thermotropic liquid crystalline polymers[J].Macromolecules,1982,15:1385-1389.
[2] Luo J D,Cheng Y J,Kim T D,et al.Facile synthesis of highly efficient phenyltetraene-based nonlinear optical chromophores for electrooptics[J].Organic Letters,2006,7:1387-1390.
[3] Song N H,Men L Q,Gao J P,et al.Cross-linkable zwittarionic polyimides with high electrooptic coefficients at telecommunication wavelengths[J].Chem.Mater.,2004,16(19):3708-3713.
[4] Gopalan P,Katz H E,et al.Star-shaped azo-based dipolar chromophores:design,synthesis,matrix compatibility,and electro-optic activity[J].J.Am.Chem.Soc.,2004,128(6):1741-1747.
[5] Shi Y Q,Zhang C.Low (sub-1-volt) halfware voltage polymeric electro-optic modulator achieved by controlling chromophore shape[J].Science,2000,288:119.
[6] Li Z,Zhao Y X,Zhou J Y,Shen Y Q.Synthesis and characterisation of a modified crosslinkable polyurethane nonlinear optical polymer[J].Adv.Mater.Opt.Electron.,1999,9:195-203.
[7] Zu F H,Qiu L,Shen Y Q,et al.Synthesis of novel second order nonlinear optical chromophore and its polyurethane polymers[J].Chem.J.Chin.Univ.-Chin.,2006,3:562.
[8] Yu Z B,Yang Z,He Y N,Wang X G,Ye C,Isocyanate crosslinked epoxy-based second-order nonlinear optical polymers[J].Acta Polym.Sin.,2004,3:345.
[9] Hao J M,Han M J,Yang Y F,et al.A device-quality thermosetting polyurethane with improved processablity and high thermal atability of dipole alignment for electro-optic applications[J].React.Funct.Polym.,2006,8:832-839.
[10] Qiu L,Shen Y Q,Hao J M,Zhai J F,et al.Study on novel second-order NLO azo-based chromophore containing strong electron-withdrawing groups and different conjugated bridges[J].J.Mater.Sci.,2004:2335-2340.
[11] Dentan V,Levy Y,Dumont M,Robin P,Chastaing E.Electrooptic polyurea waveguides by in-situ polymerization from the vapor phase[J].Opt.Commun.,1989,5-6:379-383.

[1]	税小川, 刘宇, 王跃川. “可点击”丙烯酸酯聚合物的合成及其巯-炔光交联研究[J]. 影像科学与光化学, 2018, 36(1): 82-88.
[2]	邓国伟, 陈卓, 薄淑晖, 吴杰云, 黄鹤燕, 邱玲, 甄珍, 刘新厚. 基于氢键的侧链型超分子电光聚合物的制备与表征[J]. 影像科学与光化学, 2016, 34(2): 166-171.
[3]	杨丹, 徐化君, 丛晟宇, 薄淑晖, 邱玲, 甄珍, 刘新厚. 一种以环戊并双噻吩作为π电子桥的新型发色团的合成和电光性质的表征[J]. 影像科学与光化学, 2015, 33(4): 300-306.
[4]	王志鹏, 薄淑晖, 赵文轲, 刘家磊, 王建设, 邱玲, 甄珍, 刘新厚. 高热稳定性和可逆交联性质的含新型偶氮发色团电光聚合物的研究[J]. 影像科学与光化学, 2007, 25(5): 327-332.
[5]	邱进俊, 刘承美, 包瑞, 郑启新, 郭小东. 可注射性骨修复材料不饱和聚磷酸酯的光引发交联聚合[J]. 影像科学与光化学, 2006, 24(1): 28-35.
[6]	李妙贞, 覃耀进, 常志英, 王尔鑑. AM/AMPS共聚物光化学改性[J]. 影像科学与光化学, 2002, 20(4): 247-252.
[7]	王坚, 张灵志, 陈用烈, 梁兆熙, 蔡志岗. 新型有机/无机聚合物网络的合成与二阶非线性光学[J]. 影像科学与光化学, 2002, 20(4): 276-282.
[8]	周学东, 姜永才, 张晓宏, 吴世康. 一种新型红光敏感光交联体系[J]. 影像科学与光化学, 2002, 20(3): 169-176.
[9]	高放, 徐锦旗, 李立东, 冯树京, 杨永源. 米氏酮和二苯基碘盐光产酸体系及其在印刷版材中的应用研究[J]. 影像科学与光化学, 2000, 18(4): 302-307.
[10]	陈其道, 陈明, 林天舒, 洪啸吟, 黄志齐, 胡德甫. 一种自交联聚合物的合成及其在水显影化学增幅型负性抗蚀剂中的应用[J]. 影像科学与光化学, 2000, 18(2): 155-159.
[11]	周文慧, 陈东, 林子佩, 何勇, 王尔镒. 方酸菁染料/二芳基碘鎓盐体系引发丙烯酸酯光交联反应[J]. 影像科学与光化学, 1999, 17(2): 155-158.
[12]	陈铁峰, 唐季安. 可见-红外SFG方法及其在表面和界面表征研究中的应用[J]. 影像科学与光化学, 1998, 16(1): 76-82.
[13]	曹曙光, 王仁祥, 曹维孝. 阴图PS版感光层的光交朕[J]. 影像科学与光化学, 1996, 14(1): 44-47.
[14]	李妙贞, 聂俊, 李力, 王尔鉴. 不饱和环缩醛/多硫醇体系的光交联[J]. 影像科学与光化学, 1991, 9(2): 112-119.
[15]	孟继本, 付德超, 高振衡, 姚心侃, 王宏根. 丙酮与吡咯的光诱导缩合反应[J]. 影像科学与光化学, 1989, 7(2): 71-74.

一种新型的交联极化聚合物的合成及性能研究

Synthesis and Properties of a Novel Cross-Linked Poled Polymer

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价