Ca2+、Ba2+对光敏热成像材料照相性能和稳定性的影响

doi:10.7517/j.issn.1674-0475.2005.05.367

影像科学与光化学 ›› 2005, Vol. 23 ›› Issue (5): 367-373.DOI: 10.7517/j.issn.1674-0475.2005.05.367

Ca²⁺、Ba²⁺对光敏热成像材料照相性能和稳定性的影响

林海莉^1,2, 曹静^1,2, 姚林辉¹, 夏培杰¹, 李金培¹

1. 中国科学院, 理化技术研究所, 北京, 100101;
2. 中国科学院, 研究生院, 北京, 100039

收稿日期:2005-04-04 修回日期:2005-05-11 出版日期:2005-09-23 发布日期:2005-09-23
通讯作者: 金培
基金资助:
国家自然科学青年基金资助项目(20303025).

Effects of Ca²⁺ and Ba²⁺ Ions on Sensitometric Properties and Stability of Photothermographic Material

LIN Hai-li^1,2, CAO Jing^1,2, YAO Lin-hui¹, XIA Pei-jie¹, LI Jin-pei¹

1. Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100101, P.R. China;
2. Graduate School of Chinese Academy of Sciences, Beijing 100039, P.R. China

Received:2005-04-04 Revised:2005-05-11 Online:2005-09-23 Published:2005-09-23

摘要/Abstract

摘要： 以常用的硬脂酸银为银源,异位AgBr为光敏元以及亲水型PVA为粘合剂,分别考察了Ca²⁺和Ba²⁺对光敏热成像(PTG)材料照相性能以及老化稳定性的影响.实验结果表明:涂布前乳液中加入Ca²⁺或Ba²⁺后,PTG材料的感光度和灰雾均出现不同程度的降低,并且随着加入量的增加,感光度下降更快.另外,含有Ca²⁺或Ba²⁺的PTG材料随着老化时间的增加,其感光度和灰雾的变化趋势并不相同.

关键词: 光敏热成像材料, Ca²⁺, Ba²⁺, 照相性能, 稳定性

Abstract: The effects of Ca²⁺, Ba²⁺ ion on sensitometric properties and aging stability of PTG materials, using AgSt as silver sources, ex-situ formed AgBr as photosensitive component, and PVA as binder, were investigated. The results showed that the sensitivity and the fog of PTG materials were all decreased at different degrees when adding Ca²⁺ or Ba²⁺ to system before coating, and sensitivity was debased quickly with the increase of percentage of Ca²⁺ or Ba²⁺. In addition, the changing trend of the sensitivity and the fog of PTG materials which contained Ca²⁺ was not consistent with that of Ba²⁺ as the aging time went on.

Key words: photothermographic materials, Ca²⁺, Ba²⁺, sensitometric property, stability

中图分类号:

TQ57

林海莉, 曹静, 姚林辉, 夏培杰, 李金培. Ca²⁺、Ba²⁺对光敏热成像材料照相性能和稳定性的影响[J]. 影像科学与光化学, 2005, 23(5): 367-373.

LIN Hai-li, CAO Jing, YAO Lin-hui, XIA Pei-jie, LI Jin-pei. Effects of Ca²⁺ and Ba²⁺ Ions on Sensitometric Properties and Stability of Photothermographic Material[J]. Imaging Science and Photochemistry, 2005, 23(5): 367-373.

参考文献

[1] Sakizadeh K. Antifoggants and print stabilizers for photothermographic systems based on AgX/Ag carboxylates - A review[J]. J. Imaging Sci. Techol., 2003,47:263-277.
[2] BirrEJ. Stabilization of Silver Halide Emulsions[M]. The Fcool Press, 1974.29.
[3] 范素月,彭必先.金属离子对溴碘化银乳剂微晶体的掺杂效应Ⅲ.Cu²⁺的掺杂[J].感光科学与光化学,1988,6(3):52-56.Fan S Y,PengB X.The doping effect of silver halide emulsion microcrystalsⅢ.Cu²⁺-doping[J].Photographic Science and Photochemistry,1988,6(3):52-56.
[4] 李津.锌离子在氯溴化银照相乳剂中的掺杂效应[J].感光材料,1987,(3):24-26.Li J.The effect of Zn²⁺ doped in photographic AgClBr emulsions[J].PhotosensitiveMaterial,1987,(3):24-26.
[5] 崔学福,荣惠林,等.卤化银微晶中掺杂Ca²⁺离子对其性能的影响[J].感光科学与光化学,1994,12(1):35-38.Cui X F, Rong H L, et al. The influence of doped Ca²⁺ ions on the photographic properties of silver halide emulsions[J] .Photographic Science and Photochemistry, 1994,12(1): 35-38.
[6] T ani T, Saito M. Photographic effects of metal ions I:Effects of divalent metal ions uppon emission and photographic process in silver bromide and silver iodobromide grains[J]. Photo. Sci. Eng., 1973,17(5): 434-441.
[7] 项言,王素娥.钙离子对卤化银乳剂化学增感和光谱增感的影响[J].感光科学与光化学,1992,10(2):131-137.Xiang Y, Wang Su'e. Effects of calcium ions on chemical and spectral sensitization of AgBr emnulsion[J]. Photographic Science and Photochemistry, 1992, 10(2): 131-137.
[8] George J Burgmaier, Roger L Klaus. Water soluble halogen-containing compounds[P]. US patent, 6 506 934. 2003-01-14.
[9] Maekawa T, Yoshikane M, Fujimura H, Toya I. Reaction mechanisms in thermally developed photographic systems based on silver carboxylate[J]. J. Imaging Sci. Techol., 2001,45: 365-372.
[10] Celik O, Ide S, Kurt M, Yurdakul S. Dichlordbis(phthalazine)zinc(Ⅱ)[J]. Acta Cryst., 2004, 60: 1134-1136.

[1]	徐伟华. 多层螺旋CT血管造影对冠状动脉粥样硬化性心脏病患者冠脉狭窄程度及斑块稳定性的评价[J]. 影像科学与光化学, 2020, 38(3): 491-495.
[2]	朱文庆, 樊盼, 李扬, 朱玉梦, 张瑾. 双配体Zn(Ⅱ)MOFs材料的构筑及光致发光性能[J]. 影像科学与光化学, 2020, 38(2): 159-166.
[3]	王朝兵, 李旭, 徐盼, 赵霞. 64排双源CT对T2DM合并冠心病患者冠脉狭窄程度及斑块稳定性的诊断价值研究[J]. 影像科学与光化学, 2020, 38(2): 266-271.
[4]	郭茜君, 姜小明. 光敏型季铵盐类阳离子表面活性剂的合成及表面活性和泡沫性质[J]. 影像科学与光化学, 2019, 37(3): 234-240.
[5]	陈利, 吴青阳, 刘仁, 李治全. 高稳定性巯-烯体系的深层光聚合研究[J]. 影像科学与光化学, 2018, 36(5): 408-416.
[6]	李姝静, 周自若, 岳军治, 周威, 王心蕊, 白冬生. 虎杖甙/HP-β-CD包合物的制备及光稳定性研究[J]. 影像科学与光化学, 2015, 33(6): 487-493.
[7]	李秋艳, 权莹, 梁海燕, 张乐. 化学增感对苯并三氮唑银的PTG材料感光性能的影响[J]. 影像科学与光化学, 2015, 33(3): 218-223.
[8]	石美荣, 李玉虎, 周亚军, 王朝阳, 戎岩, 贾智慧. 醋酸环境对醋酸胶片物理性能的影响研究[J]. 影像科学与光化学, 2015, 33(3): 244-250.
[9]	李波, 黄忠兵, 孟宪伟, 唐芳琼. L-半胱氨酸改性Fe₃O₄纳米粒子的水热合成及其应用[J]. 影像科学与光化学, 2014, 32(2): 163-170.
[10]	李秋艳, 李剑, 马望京, 李金培. 不同光敏剂对光敏热成像材料感光性能的影响[J]. 影像科学与光化学, 2014, 32(2): 209-215.
[11]	辛阳阳, 肖时卓, 周树云, 陈萍, 邹应全. 氨基甲酸酯乙烯基醚类化合物光聚合性能研究[J]. 影像科学与光化学, 2012, 30(6): 463-470.
[12]	陈秀英, 郭琳, 贾显林, 高海燕, 郑昌戈. 新型中位取代七甲川菁染料的合成及光稳定性研究[J]. 影像科学与光化学, 2012, (5): 375-383.
[13]	谢普会, 郭丰启, 李娟, 何勇. 新型芳香重氮盐的光与热稳定性研究[J]. 影像科学与光化学, 2012, 30(2): 118-123.
[14]	李秋艳, 孙双月, 梁海燕, 李金培. 混合银盐的光敏热成像材料感光性能研究[J]. 影像科学与光化学, 2012, 30(1): 53-59.
[15]	陈帅娜, 刘惠玉, 陈东, 吴小莉, 唐芳琼, 杨文智. 聚乙二醇功能化程度对纳米金壳夹心二氧化硅载药量及稳定性影响研究[J]. 影像科学与光化学, 2011, 29(3): 212-221.

Ca²⁺、Ba²⁺对光敏热成像材料照相性能和稳定性的影响

Effects of Ca²⁺ and Ba²⁺ Ions on Sensitometric Properties and Stability of Photothermographic Material

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价