镶嵌铂的纳米管钛酸制备及其可见光光催化活性

doi:10.7517/j.issn.1674-0475.2007.01.12

影像科学与光化学 ›› 2007, Vol. 25 ›› Issue (1): 12-17.DOI: 10.7517/j.issn.1674-0475.2007.01.12

镶嵌铂的纳米管钛酸制备及其可见光光催化活性

冯彩霞, 金振声, 王晓冬, 杨建军

河南大学, 特种功能材料重点实验室, 河南, 开封, 475001

收稿日期:2006-06-30 修回日期:2006-07-30 出版日期:2007-01-23 发布日期:2007-01-23
通讯作者: 金振声(1929-), 男, 研究员, 主要研究方向为光催化, Tel:(0378)2192331.
基金资助:
国家自然科学基金(20071010)

Preparation and Photocatalytic Behavior of Pt-inserted Nanotube Titanic Acid under Visible Light Irradiation

FENG Cai-xia, JIN Zhen-sheng, WANG Xiao-dong, YANG Jian-jun

Laboratory of Special Functional Materials, Henan University, Kaifeng 475001, Henan, P.R.China

Received:2006-06-30 Revised:2006-07-30 Online:2007-01-23 Published:2007-01-23

摘要/Abstract

摘要： 通过在真空条件下将氯铂酸的乙醇溶液引入到钛酸纳米管内,再经过热处理制备了镶嵌铂的纳米管钛酸(简写为PNTA).X射线光电子能谱(XPS)表明氯铂酸大部分转变成Pt⁰和PtO,顺磁共振谱(ESR)表明在PNTA中生成了束缚单电子的氧空位,在紫外-可见扩散漫散射谱(DRS)谱上表现出对可见光有吸收能力.丙烯的可见光光催化氧化实验结果表明:在可见光激发下(λ>420nm),PNTA对丙烯的光催化去除反应具有活性.

关键词: 铂, 纳米管钛酸, 氧空位, 可见光光催化

Abstract: Pt-inserted nanotube titanic acid(abbr.PNTA) was prepared as follows: H₂PtCl₆ ethanol solution was filled into the titanic acid nanotubes and then annealed in air at 673 K for 3 h.X-ray photoelectron spectroscopy(XPS) showed that H₂PtCl₆ has been converted to Pt⁰ and PtO.The result of electron spin resonance(ESR) revealed that there are single-electron-trapped oxygen vacancies to be formed in PNTA after heat treatment in air.Under visible light(λ>420 nm),propylene can be catalytically oxidized by PNTA in the presence of air.

Key words: Pt-inserted nanotube titanic acid, visible light photocatalysis, propylene removal

中图分类号:

冯彩霞, 金振声, 王晓冬, 杨建军. 镶嵌铂的纳米管钛酸制备及其可见光光催化活性[J]. 影像科学与光化学, 2007, 25(1): 12-17.

FENG Cai-xia, JIN Zhen-sheng, WANG Xiao-dong, YANG Jian-jun. Preparation and Photocatalytic Behavior of Pt-inserted Nanotube Titanic Acid under Visible Light Irradiation[J]. Imaging Science and Photochemistry, 2007, 25(1): 12-17.

参考文献

[1] Asahi R,Morikawa T,Ohwaki T,Aoki K,Taga Y.Visible-light photocatalysis in nitrogen-doped titanium oxides[J].Science,2001,293:269-271.
[2] Khan S U M,Al-Shahry M,Ingler W B.Jr.Efficient photochemical water splitting by a chemically modified n-TiO₂[J].Science,2002,297:2243.
[3] Nakamura I,Negishi N,Kutsuna S,Ihara T,Sugihara S,Takeuchi K.Role of oxygen vacancy in the plasma-treated TiO₂ photocatalyst with visible light activity for NO removal[J].J.Mol.Catal.A:Chem.,2000,161:205.
[4] 李伟,金振声,杨建军,张治军.纳米管钛酸的ESR特性及其可见光照的影响[J].感光科学与光化学,2003,21:273-279.Li W,Jin Z S,Yang J J,Zhang Z J.Influence of vacuum dehydration and visible light irradiation on ESR property of nanotube titanic acid[J].Photographic Science and Photochemistry,2003,21:273-279.
[5] Qian L,Jin Z S,Zhang J W,Huang Y B,Zhang Z J,Du Z L.Study of the visible-excitation luminescence of NTA-TiO₂ (AB) with single-electron-trapped oxygen vacancies[J].Appl.Phys.A,2005,80:1801-1805.
[6] Yang J J,Jin Z S,Wang X D,Li W,Zhang J W,Zhang S L,Guo X Y,Zhang Z J.Studyon composition,structure and formation process of nanotube Na₂Ti₂O₄(OH)₂[J].Dalton Transaction,2003,3898-3901,
[7] Wang T,Vazquez A,Karo A,Schmidt L D.Sulfur on noble metal catalyst particles[J].J.Catal.,1982,78:306.
[8] Hammond J S,Winograd N.XPS spectroscopic study of potentiostatic and galvanostatic oxidation of Pt electrodes in H₂SO₄ and HClO₄[J].J.Electroanal.Chem.,1997,78:55.
[9] Joint Committee on Powder Diffraction Standard,47-0124.
[10] Joint Committee on Powder Diffraction Standard,87-1286.
[11] Zhang M,Jin Z S,Zhang J W,Guo X Y,Yang J J,Li W,Wang X D,Zhang Z J.Effect of annealing temperature on morphology,structure and photocatalytic behavior of nanotubed H₂Ti₂O₄(OH)₂[J].J.Mol.Cata.A:Chem.,2004,217:203-210.

[1]	高云燕, 蔡温姣, 欧植泽, 马拖拖, 王子继, 许墨横. 苝二酰亚胺衍生物/三联吡啶铂配合物超分子在G-四链体检测中的应用[J]. 影像科学与光化学, 2017, 35(4): 552-562.
[2]	史丽娜, 曲阳, 李志君, 孙莉群, 井立强. TiO₂/Bi₂O₃纳米复合体的制备及可见光催化产氢性能[J]. 影像科学与光化学, 2015, 33(5): 426-433.
[3]	张纪伟, 金振声, 张经纬, 李秋叶, 张治军. 富含本征缺陷的新型锐钛矿TiO₂纳米管的制备[J]. 影像科学与光化学, 2015, 33(4): 285-291.
[4]	李秋叶, 金振声. 可见光“全”分解水的类纳光电化学(PEC)电池模型[J]. 影像科学与光化学, 2015, 33(2): 99-107.
[5]	段春阳, 王辉, 李凡, 张晓宏. 银纳米颗粒/聚(乙撑二氧噻吩)修饰的硅纳米线阵列的合成及可见光催化性能研究[J]. 影像科学与光化学, 2015, 33(2): 108-116.
[6]	李海燕, 钱俊杰, 刘金凤, 李秋叶, 张敏, 杨建军. 氮铋共掺杂TiO₂的合成及其可见光催化性能研究[J]. 影像科学与光化学, 2013, 31(6): 411-420.
[7]	王格侠, 冯科, 邢令宝, 史晓燕, 张丽萍, 佟振合, 吴骊珠. 4-(4-甲基-苯基)-6-苯基-2,2'-联吡啶铂(Ⅱ)光致产氢研究[J]. 影像科学与光化学, 2013, 31(1): 18-23.
[8]	樊仁杰, 陈勇, 傅文甫. 水溶性Pt(II)-Salen配合物的合成、表征和光催化制氢研究[J]. 影像科学与光化学, 2012, 30(6): 456-462.
[9]	李立, 吕小军, 迟绍明, 傅文甫. 三联吡啶铂(Ⅱ)配合物光谱性质的密度泛函研究[J]. 影像科学与光化学, 2010, 28(6): 433-441.
[10]	徐红霞, 陈彬, 吴骊珠, 佟振合. SBA-15负载多吡啶铂(Ⅱ)配合物光催化1,4-二氢吡啶衍生物的芳香化反应[J]. 影像科学与光化学, 2009, 27(5): 321-324.
[11]	王登慧, 彭明丽, 佟振合, 吴骊珠. 聚苯乙烯负载多吡啶铂(Ⅱ)配合物选择性检测Mg²⁺离子[J]. 影像科学与光化学, 2009, 27(5): 361-366.
[12]	王景菊, 王晓冬, 吴志申, 金振声. 纳米管钛酸CO处理产物的结构及光催化活性[J]. 影像科学与光化学, 2009, 27(2): 141-148.
[13]	徐占霞, 崔冠军, 张敏, 杨建军. 新型CdS/TiO₂纳米复合材料的制备及其可见光催化性能研究[J]. 影像科学与光化学, 2008, 26(6): 489-498.
[14]	马新起, 冯彩霞, 贵莉莉, 姚莉, 牛玉奇, 郭新勇. 负载银纳米管钛酸催化剂的制备[J]. 影像科学与光化学, 2008, 26(2): 104-108.
[15]	韩雪, 吴骊珠, 吴梓新, 张丽萍, 佟振合. 4-(4-甲基苯基)-6-苯基-2,2′-二联吡啶芳炔铂(Ⅱ)络合物的合成及光物理性质[J]. 影像科学与光化学, 2006, 24(3): 161-166.

镶嵌铂的纳米管钛酸制备及其可见光光催化活性

Preparation and Photocatalytic Behavior of Pt-inserted Nanotube Titanic Acid under Visible Light Irradiation

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价