低温制备具有强荧光性能三氧化钼纳米带水溶胶

doi:10.7517/j.issn.1674-0475.2012.05.384

影像科学与光化学 ›› 2012, Vol. ›› Issue (5): 384-389.DOI: 10.7517/j.issn.1674-0475.2012.05.384

低温制备具有强荧光性能三氧化钼纳米带水溶胶

张源^1,2, 吴良专¹, 余愿¹, 李豫珍¹, 只金芳¹

1. 中国科学院理化技术研究所光化学转换与功能材料重点实验室, 北京 100190;
2. 中国科学院研究生院, 北京 100049

收稿日期:2012-02-21 修回日期:2012-03-08 出版日期:2012-09-15 发布日期:2012-05-25
通讯作者: 只金芳,E-mail:zhi-mail@mail.ipc.ac.cn,Tel:010-82543537.
基金资助:
国家自然科学基金项目(20903111).

Low-Temperature Synthesis of MoO₃ Nanobelts Aqueous Sols with High Photoluminescence Properties

ZHANG Yuan^1,2, WU Liang-zhuan¹, YU Yuan¹, LI Yu-zhen¹, ZHI Jin-fang¹

1. Key Laboratory of Photochemical Conversion and Optoelectronic Materials, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, P. R. China;
2. Graduate University of Chinese Academy of Sciences, Beijing 100049, P. R. China

Received:2012-02-21 Revised:2012-03-08 Online:2012-09-15 Published:2012-05-25

摘要/Abstract

摘要： 通过过氧化途径,在低温(100℃)且不使用模板和有机溶剂的条件下,成功制备了具有良好荧光性能的三氧化钼(MoO₃)纳米带水溶胶.利用X射线衍射仪(XRD)、透射电子显微镜(TEM)、高分辨透射电子显微镜(HRTEM)、荧光光谱仪、荧光显微镜等表征手段对所制备溶胶的结构及性能进行了表征.结果显示,溶胶是由长度约为100 μm,宽度为50 nm到100 nm,厚度小于10 nm的MoO₃纳米带组成.所制备的溶胶烘干后可以得到大面积的MoO₃纳米带薄膜,薄膜具有很好的韧性.荧光光谱图及荧光显微镜照片显示,纳米带溶胶及干燥后所得到的自支撑(free standing)纳米带薄膜均具有良好的荧光性能,表明其在光学成像、传感及LED等方面具有很好的应用前景.

关键词: 三氧化钼, 溶胶, 纳米带, 薄膜, 荧光

Abstract: Colloidal molybdenum trioxide(MoO₃) nanobelts aqueous sols with high photoluminescence performance were successfully synthesized at low temperature (100℃) without assistance of any organics and templates. X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM),Fluorescence spectrameter and Fluorescence Microscope were used to characterize the structures and the properties of the as-prepared MoO₃ sols. The results revealed that the MoO₃ aqueous sol prepared is composed of a large number of colloidal MoO₃ nanobelts. The length of the nanobelts is about 100 μm, while the width is about 50-100 nm and the thickness is less than 10 nm. Large area free-standing MoO₃ nanobelts film with good toughness were obtained when the colloidal sols was dried.Its fluorescence properties were characterized by Fluorescence Microscope. The as-prepared MoO₃ nanobelts sols and free-standing MoO₃ nanobelts film both display high photoluminescence performance, which indicates their potential uses in fluorescence imaging, sensing and LED.

Key words: molybdenum trioxide, sols, nanobelts, thin-film, photoluminescence

中图分类号:

张源, 吴良专, 余愿, 李豫珍, 只金芳. 低温制备具有强荧光性能三氧化钼纳米带水溶胶[J]. 影像科学与光化学, 2012, (5): 384-389.

ZHANG Yuan, WU Liang-zhuan, YU Yuan, LI Yu-zhen, ZHI Jin-fang. Low-Temperature Synthesis of MoO₃ Nanobelts Aqueous Sols with High Photoluminescence Properties[J]. Imaging Science and Photochemistry, 2012, (5): 384-389.

参考文献

[1] Pan Z W, Dai Z R, Wang Z L. Nanobelts of semiconducting oxides[J]. Science, 2001, 291(5510): 1947-1949.
[2] Law M, Kind H, Messer B, Kim F, Yang P D. Photochemical sensing of NO₂ with SnO₂ nanoribbon nanosensors at room temperature[J]. Angew. Chem. Int.Ed. Engl., 2002, 41(13): 2405-2408.
[3] Pan Z W, Dai Z R, Wang Z L. Lead oxide nanobelts and phase transformation induced by electron beam irradiation[J].Appl. Phys. Lett., 2002, 80(2): 309-311.
[4] Dai Z R, Gole J L, Stout J D, Wang Z L. Tin oxide nanowires, nanoribbons, and nanotubes[J]. J. Phys. Chem. B., 2002, 106(6): 1274-1279.
[5] Shi W, Peng H, Wang N, Li C P, Xu L, Lee C S, Kalish R, Lee S T. Single-crystalline gallium nitride nanobelts[J]. J. Am. Chem. Soc., 2001, 123(44): 11095-11096.
[6] Gao Y H, Bando Y, Sato T. Nanobelts of the dielectric material Ge₃N₄[J]. Appl. Phys. Lett., 2001, 79(27): 4565-4567.
[7] Bae S Y, Seo H W, Park J, Yang H, Park J C, Lee S Y. Single-crystalline gallium nitride nanobelts[J]. Appl. Phys. Lett., 2002, 81(1): 126-128.
[8] Zach M P, Ng K H, Penner R M. Molybdenum nanowires by electrodeposition[J]. Science, 290(5499): 2120-2123.
[9] Zeng H C. Chemical etching of molybdenum trioxide: a new tailor-made synthesis of MoO₃ catalysts[J]. Inorg. Chem., 1998, 37(8): 1967-1973.
[10] Kim J, Lee C W, Choi W. Platinized WO(3) as an environmental photocatalyst that generates OH radicals under visible light[J]. Environ. Sci. Technol., 2010, 44(17): 6849-6854.
[11] Choi S K, Kim S, Lim S K, Park H. Photocatalytic comparison of TiO₂ nanoparticles and electrospun TiO₂ nanofibers: effects of mesoporosity and interparticle charge transfer[J]. J. Phys. Chem. C., 2010, 114(39): 16475-16480.
[12] Parida M R, Vijayan C, Rout C S, Sandeep C S S, Philip R, Deshmukh P C. Room temperature ferromagnetism and optical limiting in V₂O₅ nanoflowers synthesized by a novel method[J]. J. Phys. Chem. C, 2011, 115(1): 112-117.
[13] Hu X, Ma D, Liang J, Xie Q, Zhu Y, Qian Y. Hydrothermal synthesis of V_0.13Mo_0.87O_2.935 nanowires with strong blue photoluminescence[J]. J. Phys. Chem. C, 2007, 111(16): 5882-5885.

[1]	黄海清, 肖赛金, 杨光赵耀, 赵家辉. 氧化钼量子点无标记快速ATP检测[J]. 影像科学与光化学, 2020, 38(6): 950-955.
[2]	马逸骅, 陈琳, 杨永珍, 于世平, 苏秀琴. 钆掺杂碳量子点的制备及其双模态成像研究进展[J]. 影像科学与光化学, 2020, 38(5): 763-770.
[3]	岳帅, 邵竹梅, 姜新东. 近红外荧光BODIPY/aza-BODIPY染料的研究进展[J]. 影像科学与光化学, 2020, 38(4): 585-600.
[4]	贾红丹, 邢文莉, 宋玉姣, 郑社洪, 高云燕, 欧植泽. 负载于二氧化硅纳米粒子的菲并咪唑衍生物对Hg²⁺的检测[J]. 影像科学与光化学, 2020, 38(4): 601-608.
[5]	王佳, 王亚丽, 侯丽新, 刘贤豪. 高效钙钛矿太阳能电池吸光层的设计与优化[J]. 影像科学与光化学, 2020, 38(3): 416-423.
[6]	李箫宁, 李檬. 改性凹凸棒的制备及对砷离子的吸附研究[J]. 影像科学与光化学, 2019, 37(2): 127-135.
[7]	刘晓琴, 黄媛媛, 高建峰, 陈玉哲, 佟振合, 吴骊珠. 双光子激发的超分子聚合物纳米颗粒生物成像研究[J]. 影像科学与光化学, 2019, 37(2): 136-145.
[8]	蒋伟, 房慧颖, 何晓静. 磁共振/光学双模态分子探针的研究现状与展望[J]. 影像科学与光化学, 2019, 37(2): 156-162.
[9]	李亚丽, 郭靖, 宋娟, 朴向民, 徐晓龙, 王英平. 荧光碳点探针的合成、性质及其在生物成像中的应用[J]. 影像科学与光化学, 2019, 37(1): 46-56.
[10]	王凯霞, 徐炜, 贺庆国, 程建功. 高选择性甲基苯丙胺蒸气检测用荧光探针的设计、合成及性能[J]. 影像科学与光化学, 2018, 36(6): 478-488.
[11]	张战胜, 高杨晨, 沈敦璞, 谢垠蓬, 李明, 王猛. 铕荧光配合物的合成及其在手印显现中的应用[J]. 影像科学与光化学, 2018, 36(6): 498-506.
[12]	常顺周, 相开强, 明伟, 张志忠, 田宝柱, 张金龙. 一种基于PET机理pH荧光探针的合成及其性能研究[J]. 影像科学与光化学, 2018, 36(5): 425-433.
[13]	王娟娟, 魏学红. 温度对激光扫描共聚焦成像效果的影响[J]. 影像科学与光化学, 2018, 36(5): 443-452.
[14]	李俊芬, 李鹏霞, 张琳, 董川. 1,5-二苯基-3-联苯基-2-吡唑啉的荧光光谱行为研究[J]. 影像科学与光化学, 2018, 36(4): 299-305.
[15]	谢先格, 夏方媛, 黄苏琴, 彭小伟, 傅燕, 王筱梅, 陶绪堂. 罗丹明6G螺环酰肼荧光快速检测谷氨酸和天门冬氨酸[J]. 影像科学与光化学, 2018, 36(4): 315-323.

低温制备具有强荧光性能三氧化钼纳米带水溶胶

Low-Temperature Synthesis of MoO₃ Nanobelts Aqueous Sols with High Photoluminescence Properties

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

低温制备具有强荧光性能三氧化钼纳米带水溶胶

Low-Temperature Synthesis of MoO3 Nanobelts Aqueous Sols with High Photoluminescence Properties

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

Low-Temperature Synthesis of MoO₃ Nanobelts Aqueous Sols with High Photoluminescence Properties